邯钢无取向电工钢夹杂物演变分析.pdfVIP

邯钢无取向电工钢夹杂物演变分析 张军力 顾少伟 王小宁 鲁安平 (河北钢铁集团邯钢公司，邯郸 056015) 1 摘 要 夹杂物通过影响晶粒磁畴转动破坏电工钢产品磁性能，研究不同工艺夹杂物形成规律对提高电工钢性能有 重要意义。本文通过阐述夹杂物形成机理，利用定量金相和 SEM 能谱分析手段对邯钢无取向电工钢生产中不同工 艺环节夹杂物进行检测分析，研究不同工艺夹杂物形成规律。 关键词 夹杂物 电解 定量分析 能谱分析 Handan Iron Steel No Non-oriented Electrical Steel Inclusion Evolution Analyses Zhang Junli Gu Shaowei Wang Xiaoning Lu Anping （Handan Iron Steel Co.,Ltd. of Hebei Iron Steel Group., Handan, 056015 ） Abstract Inclusion through the influence of magnetic and then turn damage grain steel products, electrical magnetic research different process inclusion formation law to improve electrician steel performance to have the important meaning. This paper expounds the formation mechanism of inclusion, using quantitative metallographic and SEM energy spectrum analysis means of hangang no non-oriented electrical steel production in different process inclusion testing analysis, the different process inclusion formation law. Keywords inclusion, electrolysis, quantitative analysis, energy spectrum analysis 1 引言 在电工钢生产工艺过程中夹杂物主要为氧化物夹杂，包括脱氧产物和二次氧化产物。脱氧产物形成于精 炼合金化过程形成，在 RH 深脱碳后，熔渣中[O]急速向钢液传递，造成合金化后脱氧夹杂物增多。二次氧 化产物形成于精炼结束至连铸浇注过程，空气中氧进入钢水造成钢水氧化。从铸坯凝固至热轧过程，夹杂物 主要以析出形式出现，多为 MnS、AlN 等非氧化物夹杂。炼钢至热轧工艺过程中夹杂物的形成是一个连续 过程，夹杂物的尺寸、数量及组成对电工钢产品的性能有重要影响。因此有必要对邯钢电工钢生产工艺中夹 杂物进行统计分析研究夹杂物演变规律。 2 夹杂物形成机理 以脱氧产物为例，脱氧产物是钢中氧化物夹杂的主要来源，降低总氧量意味着去除氧化物夹杂。钢液温 度高，钢中元素的扩散快，脱氧元素易与钢中溶解氧作用，形成的脱氧产物由于动力学条件好，较易去除， 没有去除干净的氧化物便成为钢中氧化物夹杂的主要部分。随温度降低，钢中氧的溶解度减小，钢液中或液 固两相的液相中，过饱和的氧易在原有氧化物的基础上，与脱氧元素反应，使夹杂物长大。在合金固相线温 度以上，在液相线中形成的脱氧产物，是钢中氧化物夹杂的主要部分，尺寸通常大于 1 μm 。在钢中的氧化 .张军力，助理工程师，从事电工钢产品研发，junlizhang0625@ 第八届（2011 ）中国钢铁年会论文集