无取向硅钢50AW1300表面夹杂成因分析及控制措施.pdfVIP

无取向硅钢 50AW1300 表面夹杂成因分析及控制措施 许海亮 徐世帅 姚伟智 张洪峰 常丽芬 （鞍钢股份有限公司热轧带钢厂, 鞍山 114001 ） 1 摘 要 针对鞍钢 1700ASP 生产线无取向硅钢 50AW1300 冷轧板表面夹杂比较突出的问题，通过分析该钢种冷轧 板夹杂的基本组成与来源，对照其他牌号硅钢连铸工艺过程查找其影响因素，确定了无取向硅钢 50AW1300 冷轧 卷板表面夹杂与浇注末期塞棒头部侵蚀严重而引起的液面波动有极强的相关性；并结合生产实际情况采取一系列改 进措施，大大减少了夹杂缺陷的产生，取得了明显的效果。 关键词 无取向硅钢 表面夹杂 中薄板坯 塞棒头部侵蚀 The Causes and Control Measures of Surface Inclusions in Non-Orientation Silicon Steel 50AW1300 Xu Hailiang Xu Shishuai Yao Weizhi Zhang Hongfeng Chang Lifen (Anshan Iron and Steel Corporation Hot Strip Mill, Anshan, 114001) Abstract To solve surface inclusions in non-orientation Silicon steel 50AW1300 of An Steel 1700ASP, the composition and the source of surface inclusions in cold rolled silicon steel pates are analyzed, and influencing factors of surface inclusions are researched by comparison with casting processes of others, and the relation between surface inclusions in non-orientation Silicon steel 50AW1300 and mold level fluctuation brought by corrosion of stopper crown at the end of casting is ascertained. The corresponding control measures are put forward in combination of actual conditions, which bring about good results for cold rolled sheet surface quality. Key words non-orientation Silicon steel, surface inclusions, medium-thin slab, corrosion of stopper crown 鞍钢 1700 中薄板坯连铸连轧生产线（ASP ），是在“九五”期间的重大的、具有里程碑意义的一条短流 程热连轧生产线，是我国第一条具有独立自主知识产权的生产线，并已成功实现整体对外输出。随着鞍钢 ASP 中薄板坯连铸连轧生产线技术改造的逐渐完善和生产工艺的日臻成熟，品种规格也在不断扩大。 1700ASP 线于 2006 年 5 月开始生产硅钢，通过提高 RH 插入管使用寿命和优化精炼生产工艺等课题攻关工 作，现已成功规模化生产中低牌号无取向硅钢。生产初期存在的主要问题是，50AW100 牌号无取向硅钢表 面夹杂比较突出。夹杂废品率一度达到 0.56% 。为提高产品质量，降低夹杂发生率，有必要对无取向硅钢 50AW1300 的表面夹杂问题进行研究。 1 表面夹杂的形貌及产生原因分析 1.1 表面夹杂的形貌 该缺陷在冷轧板卷表面距边部 30~350mm 处分布，呈断续条状，宽约 1~3mm，有的附有异物，长度不 一，一般约为 30~120mm，沿带钢长度方向分布没有明显规律，如图 1 所示。