冷轧汽车板磷化膜质量检测的研究.pdfVIP

冷轧汽车板磷化膜质量检测的研究1 陈义庆 徐小连 钟 彬 肖 宇 艾芳芳 李 琳 （鞍钢股份有限公司技术中心，鞍山 114009） 摘 要 研究了利用电化学检测技术进行判定冷轧汽车板磷化膜的质量。利用恒电流/恒电位仪，测试磷化膜在磷 酸盐溶液中的开路电位与时间的关系曲线，根据该曲线出现拐点的时间来判定磷化膜的质量。研究结果显示：拐点 出现的时间t≤300s 时，磷化膜质量差；拐点出现时间300s＜t≤700s 时，磷化膜质量一般；拐点出现时间700s＜t ≤1000s 时，磷化膜质量好；拐点出现时间t＞1000s 时，磷化膜质量很好。 关键词 冷轧汽车板 磷化膜 磷酸盐 开路电位 拐点 StudyonTestingQualityofPhosphorisingFilmofColdRolled AutomobileSteelSheet Chen Yiqing Xu Xiaolian Zhong Bin Xiao Yu Ai Fangfang Li Lin （Technology Center of Angang Steel Co ．，Ltd ．，Anshan, 114009 ） Abstract Quality of phosphorising film of cold rolled automobile steel sheet is studied by electrochemical technology. The relation between open circuit of phosphorising film and time is tested in phosphate solution by constant current/potentiostat. The quality of phospharising film is determined on inflection point time of the curve. The results indicates that when inflection point time is equal to and less than 300s, the quality of phosphorising film is weak; when inflection point time is equal to and less than 700s and more than 300s, the quality of phosphorising film is common; when inflection point time is equal to and less than 1000s and more than 700s, the quality of phosphorising film is good; when inflection point time is more than 1000s, the quality of phosphorising film is excellent. Key words cold rolled automobile steel sheet, phosphorising film, phosphate, open circuit, inflection point 1 引言 磷化处理作为钢材重要的表面处理技术，在耐蚀、涂装、润滑、精饰等方面得到了广泛的发展和应用。 磷化膜质量会直接影响磷化膜在耐蚀、涂装、润滑、精饰等方面的应用效果，因此，对磷化膜质量进行检测 显得尤为重要。目前，检测磷化膜质量的方法有：膜重法、硫酸铜点蚀试验、盐水试验、电化学阻抗法和SEM 观察等。其中SEM 观察是目前检测磷化膜质量的最为直观、最令人信服的方法，但该方法需要特殊的仪器 设备，对试验环境要求高，同时操作复杂，需要专业的操作人员，因此不能广泛的应用。而其它几种方法也 存在着检测不全面、检测准确性差、数据分析复杂以及电解液易引起磷化膜质量劣变等缺点。 本工作利用电化学测试技术，探讨了采用恒电流/恒电位仪测试磷化膜在磷酸盐溶液中开路电位与时间 的关系曲线，并根据该曲线上出现拐点的时