热轧钢板常见表面缺陷浅析.pdfVIP

热轧钢板常见表面缺陷浅析 董振虎 王 焱 （济南大学控制科学与工程学院，济南 250022 ） 摘 要 随着热轧板材厚度越来越薄，使其在家用电器、汽车制造、集装箱和建筑工业等方面获得了广泛应用，热 轧薄板材在部分行业替代传统的冷轧板材已成为一种发展趋势。近年来，针对热轧板带产品愈来愈薄以及对板形精 度要求越来越高的特点，对热轧钢板的缺陷进行广泛深入的研究也变得尤为重要。本文对热轧钢板常见表面缺陷进 行了详细分类与综述，并且对产生缺陷的影响因素进行了分析。同时，对如何防止部分缺陷的产生进行了讨论。 关键词 热轧钢板 表面缺陷 缺陷分类 Analysis of Common Surface Defects in Hot Rolled Steel Plates Dong Zhenhu Wang Yan (School of Control Science and Engineering, University of Jinan, Jinan, 250022) Abstract With the thickness of hot-rolled steel plates getting thinner and thinner,it gained a wide range applications in household appliances,automobile manufacturing,container, and construction industries.Hot-rolled steel plates has become a development trend in some alternative to the traditional cold-rolled sheet metal industry.In recent years,for hot-rolled steel plates getting thinner and thinner and the increasingly high precision of the shape accuracy,it has become particularly important to extensive research for the defects of hot rolled steel sheet.Hot-rolled steel sheet classification of common surface defects are reviewed in detail, and some causes of defects are analyzed. Meanwhile, a number of hot-rolled steel plate to prevent the occurrence of defects are discussed. Key words hot rolled steel plates surface defect defect classification 1 引言 热连轧钢板、带产品是重要的钢材品种之一，随着热轧板材在各方面的应用和发展，用户对于产品的要 求也是越来越严格。而用户在注重钢板质量的同时，对于产品的外观质量也更加看重和关注。很大程度上， 外观质量是作为评价热轧钢板好坏的很重要的指标之一，如果产品的外观质量不符合要求，用户是不会认可 和接受的，因此在生产过程中，既要保证产品的性能，同时也要注重产品的外观质量。但是在热连轧产品的 整个生产过程中，由于受到一些高温、高压、高速以及硬件设备等各种因素的影响，生产出来的产品可能并 不完全符合客户的要求，钢板表面各种缺陷的产生也就不可避免