热装温度对含Nb钢高温塑性的影响.pdfVIP

热装温度对含 Nb 钢高温塑性的影响 鲁永剑 王 谦 李 江 (重庆市冶金工程重点实验室，重庆大学材料科学与工程学院，重庆 400044) 摘 要 高强度低合金钢连铸坯热送，轧制的钢板表面容易产生裂纹，成为限制此类钢种连铸坯实施热送的重要障 碍。本文在实验室利用Gleeble 试验机模拟高强度低合金钢连铸坯降温过程以及热送过程，研究了不同热送温度对 高强度低合金钢高温塑性和强度的影响，同时还就其原因进行了讨论，对预防高强度低合金钢连铸坯热送裂纹的产 生具有一定的参考价值。 关键词 高强度低合金钢 连铸坯 热送 高温塑性 Influence of Charging Temperature on the Hot Ductility of Nb-containing Steel Lu Yongjian Wang Qian Li Jiang （Chongqing Key Laboratory of Metallurgical Engineering, College of Materials Science and Engineering, Chongqing University, Chongqing, 400044 ） Abstract The hot charging of HSLA steel slabs was hindered by the cracking in HSLA steel plate surface. The influence of hot charging temperature on the hot ductility and tensile strength of a Nb-containing steel were studied by Gleeble thermal stress/train simulator. It is indicated that the hot ductility of the steel is affected obviously by the charging temperature and there is less affection on the hot tensile strength than the hot ductility. Therefore the causes for these phenomena were also discussed in present paper. Key words HSLA steel, slab, hot charging, hot ductility 1 引言 [1~2] [3] 连铸坯热送热装工艺 与传统的冷装工艺相比，具有明显的技术经济优势，统计资料表明 ，连铸坯 入加热炉温度每提高100℃，可降低燃料消耗6%左右，相对于冷装工艺，采用一般热送热装工艺可节能30%， 采用直接热送热装工艺可节能65%，采用直接轧制工艺可节能70%～80%。由于其在节能降耗方面的巨大潜 力，所以不断提高连铸坯热装率也是我国钢铁行业发展的一项重要技术目标[4] 。高强度低合金钢是近30 年 来发展最迅速、最富活力的钢类之一[5] 。由于高强度低合金钢在力学性能方面较普碳钢有着巨大的优势，被 广泛应用于建筑、重型工程结构、高压输送管道、桥梁、高压容器、汽车、集装箱、船舶、海洋平台等[6~8] 。 上述用途钢材一般占社会对钢材总需求量很大比例，所以高强度低合金钢的应用前景广阔，是现代钢铁工业 中的主力产品。但是高强度低合金钢连铸坯在采用热送热装工艺生产时，钢板表面裂纹的发生率较传统的冷 装工艺大幅度提高[9] 。 针对其形成原因以及预防