文章编号：1001-4934(2012)02-0054-05

新型冷作模具用钢的性能及热处理

于波

(常州机电职业技术学院模具技术系，江苏常州213164)

摘要：介绍了国内外冷作模具用钢的发展概况和趋势，对新型冷作模具用钢的性能与热处理进行了较详细的阐述，并针对我国今后模具钢的研发进行了展望。提高模具钢的冶炼技术，以保证模具钢的性能要求，开发与完善模具材料系列，正确选用热处理技术，改善模具的冷热加工工艺，提高了产品质量和模具寿命。

关键词：冷作模具钢；性能；热处理

中图分类号：TG162.4文献标识码：B

Propertiesandheattreatmentofnewcold-workingdiesteelsYUBo

Abstract:Thedevelopmentsurveyandtrendofcold-workingdiesteelsbothathomeandabroadwereintroduced,andthepropertiesandheat-treatmentofthenewcold-workingdiesteelswereexpoundedindetail,thenthefuturedevelopmentprospectofthediesteelsinourcountryweregiven.Thesmeltingtechnologyofthediesteelsshouldbeimprovedtoguaranteethepropertyrequirements,andthematerialseriesofdieshouldbedevelopedandperfected.Meanwhile,theheattreatmenttechnologyshouldbeselectedaccurately,andthecoldandhotworkingprocessshouldbeimprovedtoenhancetheproductqualityanddielife.

Keywords:cold-workingdiesteels;property;heattreatment

0引言

随着工业生产技术的发展和不断出现的新材料，冷作模具的工作条件日益苛刻，对冷作模具的性能、质量和品种提出了更高、更新的要求，为了适应不同模具的特殊性能要求，各国的模具工作者除对传统的模具材料不断开发新的热处理工艺外，还不断开发具有不同特性以适应各种性能要求的新型冷作模具材料。各国有针对性地发展了一些新型的模具钢。

目前世界上通用的冷作模具钢分3类：(1)

收稿日期：2011-05-06

作者简介：于波(1959一),男，教授。

低合金冷作模具钢，以美国ASTMA681标准中的O1(9CrWMnV)为代表；(2)中合金冷作模具钢，以A2(Cr5MolV)钢为代表；(3)高合金冷作模具钢，以D2(Cr12MolV1)钢为代表，此外还研制了一些新型冷作模具钢。

目前，我国常用的冷作模具钢仍然是低合金工具钢CrWMn、高碳高铬钢Cr12和Cr12MoV等传统的典型钢种。CrWMn钢虽然具有一定的的淬透性，淬火变形小，但是其韧性、变形要求等仍不能满足形状复杂、大型和受冲击负荷大的冷作模具的需要。而且锻后需较

模具技术2012.No.255

严格的控制冷速，否则易形成网状碳化物，导致模具在使用中崩刃和开裂，Cr12型钢具有很高的耐磨性，但其碳化物不均匀性比较严重，特别在其尺寸较大时，反复镦拔收效不大，导致变形的方向性和强韧性降低，使用中