2018年第3期 工业、生产 气相法聚丙烯主要生产工艺及催化剂技术 任春红 中国石油化工股份有限公司北京化工研究院 北京 100013 摘要：综述了近年来聚丙烯生产气相工艺的研发和进展，以及国内相应的引进厂家及对应产能。目前气相工艺的主要 代表有Spherizone工艺、unipol工艺、Novolen工艺、Innovene工艺等，同时综述了工艺配套催化剂及国产催化剂在生产工艺 上的应用进展，并展望了国产催化剂的开发应用前景。 关键词：齐格勒-纳塔  聚丙烯  气相工艺  综述 The Main Production Process of Gas Phase Polypropylene and Catalyst Technology Ren Chunhong  1Beij ing Research Institute of Chemical Industry (BRI CI) , China Petroleum Chemical Corp oration, Beij ing, 100013, China Abstract：In this paper, the research and development of gas phase process for polypropylene in recent years are summarized.  And corresponding domestic manufacturers and corresponding production capacity are introduced. At present, the main representatives  of the gas phase process are Spherizone, unipol, Novolen and Innovene. At the same time, Process combined catalysts and the progress  of application of domestic catalysts in the production process are introduced. The prospects for the development and application of  domestic catalysts are also forecasted. Keywords：Ziegler-Natta；Polypropylene；Gas phase process；Summary 聚丙烯，尤其是等规聚丙烯具有优良的物理、化学、 可生产组成和结构精准设计的丙烯均聚和无规共聚物[16] ， 机械及电绝缘性能，如低密度、而腐蚀、易加工及经济性 还能实现双峰聚合物的生产，可以获得更加均匀的聚丙烯 等，近年来应用非常广泛[1， 2] 。聚丙烯的生产工艺按聚合 产物，提高其熔体强度和抗冲性能，并能改善产物的蠕变 类型分类有本体法工艺、气相法工艺、溶液法工艺和溶剂 和加工性能[15] 。上升区下降区中的聚合物堆积密度不同， 浆液法工艺(简称浆液法，也称淤浆法)，后两者主要是早 在上升区中可达40%，而在下降区中则可达到90%。高堆 期的工艺，现在主要有本体法工艺和气相法工艺及其组 积密度使聚合物从下行区排出时未反应物的排放减少，减 合工艺[3] 。本体法工艺反应器可以为环管或搅拌釜，气相 少脱气回收气体时所需的能量[17] 。多区反应器配套气相反 法工艺反应器有立、卧式搅拌床或流化床。主要的代表有 应器还可生产抗冲聚丙烯树脂。国内采用该工艺的主要 LyondellBasell公司的Spheripol（本体+气相）和Spherizone 有[6] ：中沙（天津）石化，2006年