工业钛钨粉-SCR催化剂的制备及表征-化学专业论文.docxVIP

重庆大学硕士学位 重庆大学硕士学位论文 英文摘要 PAGE PAGE VI by domestic industrial titanium tungsten powder was reduced to 95% during 300~350℃，but catalytic performance of catalyst prepared by imported industrial titanium tungsten powder was hardly affected, which was higher than 99%. Added Na2O to V2O5-WO3/TiO2 catalyst, change rule of catalytic activity of V2O5-WO3/TiO2 catalysts prepared by different methods with different concentration of Na2O was opposite; Added Fe2O3 to V2O5-WO3/TiO2 catalyst, catalytic activity of 20Fe2O3-V2O5-WO3/TiO2 catalyst prepared by multistep impregnation method was significantly reduced during 350~450℃, but catalytic activity of catalyst prepared by one-step impregnation method hardly affected the catalytic performance. Keywords：SCR, V2O5-WO3/TiO2 catalyst, industrial titanium tungsten powder (WO3/TiO2) 重庆大学硕士学位 重庆大学硕士学位论文 目 录 目 录 中文摘要I 英文摘要 II 1 绪 论 1 1.1 氮氧化物的来源及危害 1 1.2 氮氧化物的控制技术 2 1.2.1 吸收法 2 1.2.3 选择性非催化还原(SNCR)技术原理 3 1.2.4 选择性催化还原(SCR)技术 3 1.3 V2O5-WO3/TiO2 催化剂的组成 5 WO3/TiO2 5 V2O5 6 1.4 V2O5-WO3/TiO2 催化剂的制备工艺 7 1.4.1 浸渍法 7 1.4.2 溶胶凝胶法 8 1.4.3 混合法 8 1.5 碱金属对 V2O5-WO3/TiO2 催化剂活性的影响 9 1.5.1 K2O 对 V2O5-WO3/TiO2 对催化剂性能的影响 9 1.5.2 Na2O 对 V2O5-WO3/TiO2 对催化剂性能的影响 9 1.6 本论文的主要研究内容 10 2 实验部分 11 2.1 实验试剂与气体 11 2.2 实验设备 12 2.3 催化剂的脱硝率测试 12 2.4 催化剂 SO2/SO3 转化率的测试 12 2.5 催化剂的表征 14 2.5.1 BET 比表面积和孔结构 14 2.5.2 X 射线衍射（XRD） 14 2.5.3 傅里叶红外光谱（FT-IR） 14 2.5.4 热分析（TGA） 14 2.5.5 扫描电子显微镜/X 射线能谱（SEM/EDX） 14 3 V2O5-WO3/TiO2 催化剂原料及组成的研究 15 HYPERLINK \l _TOC_250012 3.1 WO3-TiO2 催化剂的研究 15 HYPERLINK \l _TOC_250011 3.1.1 WO3-TiO2 催化剂的制备 15 HYPERLINK \l _TOC_250010 3.1.2 WO3-TiO2 催化剂的脱硝率 16 HYPERLINK \l _TOC_250009 3.1.3 WO3-TiO2 催化剂的表征 16 3.2 V2O5 含量对 V2O5-WO3/TiO2 催化剂脱硝性能的影响 20 3.2.1 不同 V2O5 含量的 V2O5-WO3/TiO2 催化剂的制备 20 3.2.2 不同 V2O5 含量的 V2O5-WO3/TiO2 催化剂的脱硝率 21 3.2.3 不同 V2O5 含量的 V2O5-WO3/TiO2 催化剂的表征 22 HYPERLINK \l _TOC_250008 3.3 WO3 含量对 V2O5-WO3/TiO2 催化剂脱硝性能的影响 24 HYPERLINK \l _TOC_250007 3.3.1 不同 WO3 含量的 V2O5-WO3/TiO2 催