低合金中厚板探伤不合原因分析及对策_宽厚板_2009tr.pdfVIP

第l5卷第4期 宽厚板 VoI．15．No．4 · 6·2009年8月 WIDE AND HEAVY PLATE August 2009 · 生产实践 · 低合金中厚板探伤不合原因分析及对策 王 杰 鞠传华 陈福山 王新刚 乔孟平 (济南钢铁股份有限公司) 摘 要 通过低倍、金相及扫描电镜等手段，对引起低合金中厚板探伤不合的原因进行分析，阐明了铸坯 内部中心偏析、夹杂物及微裂纹是导致钢板探伤不合的内在原因，在生产中采取相应措施，可有效提高钢板探 伤合格率。 关键词 低合金中厚板 超声波探伤 偏析 微裂纹 Analysis on the Causes of Nonconformity in Ultrasonic Flaw Detection of Low Alloy Me~um Steel Plate and Countermeasures to be Taken Wang Jie，Ju Chuanhua，Chen Fushan，Wang Xingang and Qiao Mengping (Jinan Iron and Steel Co．Ltd) Abstract By using methods of macrostructure examination，microstructure examination and SEM ，the causes of the nonconformity in ultrasonic flaw detection of low alloy medium steel plate has been investigated．It is explained that the central segregation，inclusions and microcrack inside the strand are the internal causes of nonconformity in the ul— trasonic flaw detection on the steel plate．The conformity ratio of the steel plate ultrasonic flaw detection call be effec— tively improved by taking relevant measures in production． Keywords Low alloy medium steel plate，Ultrasonic flaw detection，Segregation，Micro—crack 0 前言 轧制方向，呈间断分布的长条形缺陷，这种缺陷 随着钢板厚度的增加，用户除要求外在质量 虽然可以通过切边解决，但容易造成钢板宽度不 和力学性能外，绝大多数要求增加探伤检验，通过 合改判；另一种是分布在板宽1／4～1／2区域的 超声波探伤可以检测出钢板内部的质量缺陷，从 点状密集缺陷，缺陷的类型主要是偏析，部分钢 板存在分层现象。这两种缺陷有时在钢板上单独 而优选出高质量钢板。某钢厂低合金中厚板在超 声波探伤检验时，因探伤不合造成产品改判或报 存在，有时同时出现。 废的现象时有发生，在一定程度上影响了产品交 2 分析与讨论 货期及合同兑现率。本文通过低倍、金相及扫描 2．1 中心偏析 电镜等手段，对引起低合金中厚板探伤不合的原 对探伤不合格的钢板进行低倍酸浸检验，发 因进行分析，并提出解决此类问题应采取的工艺 现试样厚度中心位置存在偏析，如图1。钢水冷 措施。 却过程中，结晶时往往形成枝晶偏析