集装箱角件材料低温冲击韧度的研究.pdfVIP

学兔兔 铸造工艺 集装箱角件材料低温冲击韧度的研究 徐小玉 (常州轻工职业技术学院，江苏 常州21 31 64) 摘要：集装箱角件的低温冲击韧度非常重要。通过改变炼钢过程脱氧工艺，减少夹杂物量，改 变夹杂物类型；另一方面调整其后期热处理工艺，使得ZGI5Mn铸钢材料晶粒细化，从而提高该 类钢材的低温韧度，满足集装箱角件的性能要求。 关键词：集装箱角件；低温冲击韧度；脱氧变质处JE；热处理工艺 中图分类号：TG142．1 2 文献标识码：A 文章编号：1673-3320(2009)04—0013—03 Study on Low Temperature Impact Toughness of Corner Casting for Container Xu Xiaoyu (Changzhou Institute of Light Industry Technology,Changzhou 2 1 3 1 64，Jiangsu，China) Abstract：It is critical to low temperature impact toughness of comer castings for container．The inclusion content was decreased and inclusion types were changed through adjusting the deoxidization and modification．The grain size of comer castings was refined through modifying heat treatment process． The low-temperature impact toughness was improved，and the performance of comer casting of container was satisfied． Key words：corner casting for container；low temperature impact toughness；deoxidization and modification；heat treatm ent process 由于集装箱运输具有方便、简捷、安全等特 后期热处理工艺，使得集装箱角件晶粒细化，从 点，在货物运输业中占有重要的地位。常用的船 而提高材料的低温韧度，以满足集装箱角件的性 用集装箱允许堆码达六层，每只装载量可达40 t， 能要求[ 】。 且要经受海浪颠簸；在寒带地区起吊时还需防脆 1 试验方法及内容 断。因此作为主要配件的集装箱角件，必须具备 我国对于制造角件的材料有严格的要求，每 一 定的强度和低温韧度。同时由于集装箱需要堆 炉铸钢件均应按国家标准的规定进行化学分析和 码、搭扣和起吊，因此其角件的形状非常复杂多 力学性能试验，表1列出了各国角件的化学成分标 样。为满足使用性能要求，通常采用铸造成形的 准。作为特殊用途的钢材，其化学成分有一定的 方法，通过控制其化学成分和热处理工艺来生 碳当量要求，应不大于0．42％；如果碳含量低于 产。 0．