铝合金三价铬钝化液的研制和应用.pdfVIP

学兔兔 铝合金三价铬钝化液的研制和应用 熊 鹰 ，彭敬东z (1．重庆长江造型材料集团有限公司，重庆400715；2．西南大学化学化工学院，重庆400715) 摘要：分析了铝合金三价铬钝化液的钝化机制，研究了复合盐钝化剂用量、钝化处理时间和温 度对钝化膜质量的影响。结果表明，经铝合金三价铬钝化液钝化后的试样，其抗腐蚀性能优于 铬酸钝化液，可在常温下进行处理，且处理时间较短，有利于减轻铬酸钝化液中六价铬离子对 环境的影响。 关键词：铝合金；表面钝化；三价铬钝化液 中图分类号：TG1 74．4 文献标识码：A 文章编号：1673-3320(2010)05-00014-02 Development and Application of Trivalent Chromium Passivator for Aluminum Alloy Xiong Ying’，Peng Jingdong (1．Chongqing Changjiang Moulding Material Group Co．，Ltd．，Chongqing 40071 5，China； 2．School of Chemistry and Chemical Engineering，Southwest University,Chongqing 40071 5，China) Abstract：The passivation mechanism of trivalent chromium passivator for aluminum alloy has been studied，including additive amount of complex salt passivator,influence of processing time and temperature on the quality of passive fllm．The test has shown that the samples treated by trivalent chromium passivator has improved anti．corrosion property．The treat process is at room temperature and quite short．The impact on environment can be reduced without hexavalent chromium acid． Key words：aluminum alloy；passivation；仃ivalent chromium passivator 铝在全球的产量仅次于铁。铝及铝合金具有 因如此，有机涂膜下的铝合金基体一经腐蚀，涂膜 诸多优点，如比强度高、导热和导电性好、反光性 与基体间结合力的丧失就远超过钢铁件。 强、色泽美观、无磁性、耐蚀性和成形性好等等。 提高有机膜结合力，降低涂膜下基体腐蚀的 因此铝及其合金在汽车、摩托车、飞机和船舶等工 主要措施是使其表面生成一种能耐pH变化的转化 业中得到广泛应用。 膜。用作涂装的转化膜主要有：阳极转化膜、铬酸 盐转化膜、铬酸盐一磷酸盐转化膜、钛或锆盐转化 铝及其合金在大气环境中会自动形成一层极 膜、非铬氧化膜、磷化膜等。阳极氧化膜的优点是 薄的天然氧化膜，厚度仅为0．4～0．5 nm。这层氧化 耐磨和可用于