纳米复合及表面改性铸型醇基粉状涂料的研究.pdfVIP

学兔兔 纳米复合及表面改性铸型醇基粉状涂料的研究 孙鲁洪，胡吴民，楼建余，章 霖 (深圳市景鼎现代科技有限公司，广东 深圳 518117) 摘要：为改善醇基粉状涂料的悬浮稳定性，采用纳米复合和表面改性技术制备了系列醇基粉状 涂料。通过扫描电镜考察了粉状涂料的微观形貌，并进行了涂料的实际浇注试验。分析和试验 结果表明：研制的醇基粉状涂料无须引发，加醇搅拌后即能制得具有良好悬浮稳定性的浆状涂 料；浇注的铸件表面光洁，无粘砂等缺陷。 关键词：醇基粉状涂料；纳米复合；表面改性 中图分类号：TG221 文献标识码：A 文章编号：1673-3320(2010)06-0001-04 Study on Nano-composite and Surface Modification of ‘ Alcohol-base Powder Coatings for Sand Casting Sun Luhong，Hu Haomin，Lou Jianyu，Zhang Lin (Shenzhen King-top Modern Hi—tech Co．，Ltd．，Shenzhen 518117，Guangdong，China) Abstract：To improve the suspension．the alcohol—base powder coatings were prepared by nano． composite and surface modification technology．The morphology of powder coating was investigated by SEM．and the field．test of pouring castings was carried．The results show that the alcoho1．base powder coatings have no initiation．and the ready—for-use coatings with beRer suspensible stability are made by adding alcohol directly．The surfaee of castings is smoother and cleaner,and free of burning—on sand． Key words：alcoho1．．base powder coating；nano．．composite；surface modification 随着对铸件表面品质的要求日渐提高，水 本没有可以稳定使用的产品。因此，开发研制醇 玻璃砂和树脂砂等化学黏结剂被广泛采用，由此 基粉状涂料对于满足国内外市场的需求具有较大 具有点火燃烧、涂层强度高、不需烘干等优点的 的现实意义。 醇基涂料受到了更多的关注。目前商品化的醇基 1 醇基粉状涂料组分选择 涂料绝大多数以浆 (膏)状形态供货。醇基涂料 属易燃危险品，这就不可避免地使其在包装、运 1．1 耐火粉料 输、贮存等方面受到诸多约束，尤其是运输周 耐火粉料是涂料的主要组成部分，也是最终 期长，费用高；此外由于醇基涂料悬浮稳定性较 在金属一铸型界面上起作用的骨干材料【2]。耐火粉 差，涂料在长途运输和存放过程中易分层，使其 料对涂料的抗粘砂能力起决定性作用，它的物理 工艺性能下降，严重时涂料产生板结 (死沉淀) 和化学性能在很大程度上决定了涂料的性能。涂 现象而报废…。目前已有少数涂料生产企业研发 料中耐火粉料应根据铸造合金的种类确定。通过 出醇基粒状涂料，但由于悬浮剂的引发问题未得 分析选用的耐火粉料性质及其适用合金如表1