现代规模化生产中铬铸铁磨球新工艺.pdfVIP

学兔兔 铸造工艺 现代规模化生产中铬铸铁磨球新工艺 刘保根，王仲珏 (安徽工程科技学院，安徽 芜湖 241000) 摘要：根据磨料介质的实际服役工况条件，生产中铬白口铸铁磨球的工艺设计原则应明确为： 在改善韧度指标的前提下，进一步提高硬度。以在实践中成功运用的实例，从控制冷速、成分 设计、铸造冶金处理和热处理等方面介绍了新工艺，并指出该工艺适合现代工业的规模化生产 方式，具有较强的市场竞争力。 关键词：中铬白口铸铁；磨球；规模化生产 中图分类号：TG143．1 文献标识码：A 文章编号：1673—3320(2009)04—0009—04 A New Technique Adapt to Scale Modern Production of Medium Chromium Cast Iron Grinding Ball Liu Baogen，Wang Zhon~ue (Anhui University of Technology and Science，Wuhu 24 1 000，Anhui，China) Abstract：Considering practical use condition．the process design priciples of medium chromium white cast iron production should be defined to further enhance the hardness under the premise for improving the toughness．By the examples used in practice successfully,the new process including cooling rate contro1．composition design．metallurgy and heat treatment was introduced．It iS pointed out that the process with s~ong market competitiveness is suitable for the large．scale modem industrial production． Key words：medium chromium white cast iron；grinding ball；scale production 中铬白口铸铁磨球的组织可以被看成是海绵 · 1．1 组织 网状并镶嵌奥氏体的转变物M，C型渗碳体，以及 铸态组织：马氏体+适量残余奥氏体+M，C3 呈三维开放式骨架分布的M C，型为主的合金碳化 为主+断网及条粒状的M3C+MC；亚温处理的组 物的混合物。因此，其强度和韧度就取决于脆性 织：马氏体+少量残余奥氏体+M，C，+断网及条 M C碳化物相的体积分数和分布形态。结合大多 粒状的M C+MC。这主要是基于下列考虑： 数的服役工况条件，应将中铬白口铸铁磨球在获 1)铸铁的抗磨性和韧度随碳化物的种类变 得较好韧度的前提下，进一步提高硬度作为工艺 化，按M3C、M7C3、MC~ iJ而明显提高；碳化物 设计的指导原则。该类磨球工艺的要点可以概括 组成及形态对导热率及热扩散率影响最大，粗大 为：①获得尽可能多的M，c，合金碳化物；②改变 网状的M C碳化物的导热率、热扩散率最差；碳 M，C碳化物形态；③在获得马氏体基体的同时，