球化处理过程中提高喷镁吸收率的途径.pdf

铸 造 Feb．2012 学兔兔 FOUNDRY V0I．61 N0．2 球化处理过程中提高喷镁吸收率的途径 冯光弼，刘 菲 (安钢集团永通球墨铸铁管有限责任公司，河南安~n455133) 摘要：在球墨铸铁生产中，随着喷吹钝化颗粒镁脱硫球化工艺的投产使用，如何提高镁的吸收率，是当前降本增效的 关键措施之一。通过对金属镁的物理化学性质的分析认为：镁的吸收率与铁液的成分、温度、喷吹的载体以及喷枪气 化室与铁液液面的高度等有关。 关键词：喷吹；钝化镁；脱硫球化 中图分类号：TG255 文献标识码：B 文章编号：1001—4977(2012)02—0192—03 Method of Improving Absorptivity of Injection Magnesium During Spheroidizing Process FENGGuang—bi，LIUFei (Angang Group Yongtong Ductile Cast-Iron Co．，Ltd．，Anyang 455 1 33，Henan，China)、 Abstract：For the desulphurising and nodularizing process by passivation magnesium grain injection，how to improve the magnesium absorptivity of meIt iron iS a key measure for reducing cost and increasing emciency． According to the physical and chemical properties of magnesium，it was concluded that magnesium absorptivity is related to composition and temperature of molten iron．injection equipment and the height between the gasification chamber Of airbrush and liquid level of melted iron． Key words：injection；passivation magnesium；desulphurization and nodularization 在铁液炉外脱硫中，镁系脱硫具有单耗低，渣量 少，速度快，温降小，脱硫能力强且稳定，防止回硫、 环境污染小等优点。钢铁企业采用喷吹钝化镁进行脱硫 的技术已经非常成熟。近年来，许多球墨铸管生产厂家 也开始使用喷吹钝化镁进行球化处理替代原来的冲人 法、喂丝法球化工艺，大幅度降低了球铁管的生产成 本，原材料质量稳定，而且比原来更好控制。新工艺投 入使用之后，镁的吸收率为25％～35％，如何提高镁的 吸收率，进一步降低成本是厂家一直面临的难题。 1 喷吹钝化颗粒镁的原理 喷吹钝化镁脱硫、球化原理是由镁粒储存罐通过 干燥的工业氮气作为载体，由喷粉管携带钝化镁颗粒， 1．氮气储存罐 2．压力阀 3．流量计 4．减压阀 5．罐压力阀 经过喷枪将钝化镁连续稳定地输入铁液中，镁粉在喷 6．镁粒储存罐 7．混合室 8．喷吹开关 9．喷吹软管 l0．氮气管 枪气化室内气化后，镁蒸汽在铁液里上浮过程中不断 11．包盖 l