学兔兔 压铸锌合金用三价铬钝化液的开发和应用 汪晓琴，石 燕 (西南大学化学化工学院，重庆 40071 5) 摘要：分析了一种高效、环保压铸锌合金用三价铬钝化液的主要成分及其操作工艺条件，优化 了钝化液工作的参数，包括钝化液pH值、钝化温度和钝化时间的影响。研究结果表明，经三价 铬钝化液处理后的锌合金，其钝化膜层均匀，色泽白亮、略显淡蓝色，耐中性盐雾腐蚀时间超 过96 h；该三价铬钝化液不仅有利于减轻原六价铬钝化液中六价铬对环境的污染，而且价格便 宜、操作工艺简单。 关键词：压铸锌合金；三价铬钝化液；表面处理 中图分类号：TG1 74．42 文献标识码：A 文章编号：1673—3320(2014)06—0020—03 Development and Application of Trivalent Chromium Passivant for Zinc Diecast Alloy WANG Xiaoqin，SHI Yan (School of Chemist~and Chemical Engineering，Southwest University，Chongqing 40071 5，China) Abstract：The main ingredients and operating conditions of a high efficient and environmentally friendly trivalent chromium passivant for zinc diecast alloy were analyzed．The process parameters of passivant were optimized including the effects of pH，passivating temperature and time．The results show that after passivating treatment，the film of zinc alloy colored with light blue is uniformly and it can resist to neutral salt more than 96 hours．The trivalent chromium passivant for zinc diecast alloy is not only beneficial to reduce the pollution of hexavalent chromium，but alSO cheap and with simple operating conditions． Kev words：zinc diecast alloy；trivalent chromium passivant；surface仃eatment 锌在地壳中的含量为0．01 3％，是重要的金 属及其合金材料上。传统的钝化处理大多以铬酸 属原材料，其产量和消耗量在铁、铝和铜之后， 和铬酸盐等六价铬化合物为处理剂，经钝化处理 居第四位。锌合金由于具有诸多优点，例如熔点 后在金属表面上形成的铬酸盐转化膜对基体金属 低、流动性好，易熔焊和可塑性加工等，因此 具有良好的防蚀性能。然而，六价铬被公认为是 具有广泛的用途。但是，锌的钝性系数较低，仅 一 种毒性极强的致癌物质，也是严重污染环境的 0．024，故在自然状态下，锌合金自动形成的氧 重金属之一；六价铬在自然界中不能自然降解， 化膜疏松、