新型氟硅改性二氧化硅消光剂的性能及应3-2.docVIP

新型氟硅改性二氧化硅消光剂的性能及应用 The properties and applications of a novel fluorine-silicon modified silica matting agent 李先文① 王小强② 朱葛中② （①无锡高宗粉体材料有限公司，江苏宜兴化工市场广汇北路24-401，电话： 0086传真：0086-0510email：603376913@。②江苏三木集团设计院） 摘要：本文介绍了一种用有机氟硅材料进行表面改性的新型无机二氧化硅消光剂，它不但有干滑的手感、还具有与大多数有机高分子材料相容性佳，分散性好的特点。该消光剂有较高的吸油值但却极大地控制了增稠和触变。它保持了有机氟硅的优良特性和大孔硅胶的消光性，在涂料特别是UV涂料油墨中得到很好的应用。 关键词：氟硅化合物、消光性、粘度、吸油值、干滑、相容性 Abstract：This paper mainly describes a novel kind of fluorine-silicon modified silica matting agent which has not only dry-slip feel, but also good miscibility and dispersibility with most kind of polymer material. Moreover, the matting agent has high oil adsorption but maintain a viscosity profile suitable for application at the addition levels required for good matting. Furthermore, it bears porous structure characteristics as well as excellent matting properties and thus it can be widely used in UV coatings and ink systems. Key words：fluorine-silicon、matting、Viscosity, oil absorption value, dry sliding, compatibility 前言 二氧化硅消光剂因其折光系数与涂料工业中使用的大部分树脂的折光系数相近（1.46），而具有良好的光学性能，目前广泛用于涂料中，成为高档涂料消光剂的首选。二氧化硅消光剂主要有大孔硅胶、沉淀白炭黑和气相二氧化硅三种。大孔硅胶的化学组和物理结构，决定了它具有许多其它同类材料难以取代的特点：吸附性高、热稳定性好、化学性质稳定、。R1R2(SiO)xR3+HO(SiO2)y 催化剂 R1R2(SiO)x R3O(SiO2)y+R4 其中： R1和R2可以为-CnFm(1≤n≤3，1≤m≤6)，-CkH2k+1（1≤k≤50），-CbH2b（1≤b≤50） R3：OH，NO2、 NH2、 COOH、 HS、 Cl、 OCH3、OC2H5、C6H5O。 R4：H2O、NH3、 HCl、 H2或无。 1≤x≤1000， y≥1。 工艺流程： 水玻璃稀释 　　净化 硫酸稀释 沉淀反应 过滤洗涤　 浆化　 有机氟助剂 　 搅拌 有机硅助剂　 浆化 喷雾干燥　　 基 料 　除铁除凝胶颗粒　 机械粉碎　 气流粉碎 　 气流分级 　 自动包装 工艺阐述： 1. 大孔硅胶生产 经过严格除铁除杂净化处理后的液体硅酸钠稀释到需要的浓度后，在60-100℃下，将一定浓度的硫酸按需要的流速加入，生成的二氧化硅在不同的温度和浓度条件下，晶粒不断长大，加入适当的扩孔助剂并通过严格的扩孔工艺，使晶粒聚集形成大孔多孔结构硅胶微粒，生成的二氧化硅硅胶微粒，经过压滤反复洗涤，除去硫酸盐，最后经过打浆机浆化。 2．表面改性处理 在已经浆化好的悬浊液中首先加入有机氟助剂，搅拌均匀后加入有机硅助剂，进行第二次高强度浆化处理，使助剂和浆液充分混合均匀，然后喷雾干燥，控制干燥温度，在干燥的过程中实现同步活化，完成表面改性处理。 3．超细粉碎 将表面改性处理后的有机氟硅二氧化硅进一步除铁除凝胶颗粒（来源于极少很难被浆化的高强度凝胶颗粒）进行机械粉碎，将大颗粒破碎，然后进行气流粉碎，通过严格的分级系统，达到要求的小微粒进入收集器，大微粒被返回继续粉碎，该过程实现了很窄的粒径分布。最后进行自动真空