40907065+李吉文+化学+钛酸铜钙-苯乙烯复合材料的制备及性能研究.docVIP

分类号： 陕西师范大学学士学位论文 作 者 单 位 化 学 化 工 学 院 指导教师（职称） 教授作 者 姓 名 专 业、 班 级 化 学 2009级2 班 提 交 时 间 二 〇 一 三 年 六 月 710062） 摘要：本论文采用原位聚合法制备了钛酸铜钙/聚苯乙烯复合材料。X射线衍射、扫描电子显微镜、阻抗分析仪研究了对性能的影响。结果表明： 关键相结构 介电This paper was prepared by in-situ polymerization method copper calcium titanate/polystyrene composite materials. Using X-ray diffractometer, scanning electron microscope, the impedance analyzer and infrared spectrum to corresponding characterization of composite materials such as copper titanate ceramic filler is studied the effect of calcium on the properties of composite materials. Results show that the composite material, CCTO can be spread more evenly in the styrene substrate. With the increase of ceramic packing, the dielectric constant increases. The maximum dielectric constant (15) of composite materials at 1 kHz obtained when the filler content reached 50%, which is 5 times of matrix. Dielectric constant of the composite material is larger than that of matrix has been further improved. Keywords: Copper Calcium Titanate，styrene，phase structure，composite material， dielectric properties 目 录 摘要 ABSTRACT Ⅰ 1 前言 2 实验内容 2.1 CCTO陶瓷粉体的制备 4 2.1.1 实验原料及仪器 4 2.1.2 具体制备过程 5 2.2 PS/CCTO复合材料的制备及其性能研究 5 2.2.1 主要实验原料 5 2.2.2 主要实验仪器 6 2.2.3 主要分析测试方法与测试仪器 6 2.2.4 实验步骤 6 3 实验结果与讨论 3.1复合材料红外光谱分析 6 3.2复合材料的相结构分析 3.3复合材料的微观形貌分析 8 3.4复合材料的介电性能测试 9 4 结束语 12 【参考文献】 致 谢 1 1前言 图1-1 现如今高介电常数的电介质材料以无机陶瓷材料为主，如钛酸钡()、钛酸锶(SrTiO3)、钛酸锶钡(Ba0.65Sr0.35TiO3)、(PbTiO3)、铌镁酸铅-钛酸铅(Pb(Mg1/3Nb2/3)O3-PbTiO3)。但由于陶瓷材料固有的弱点，如为开发新型提供实验指导和新思路。2 实验内容 2.1 C16H36O4Ti：天津市津科精细化工研究所 稀氨水：自配 冰醋酸：化学纯 无水乙醇：化学纯，北京益利精细化学品有限公司。 仪器：电子天平：BSA224S-CW，赛多利斯科学仪器（北京）有限公司。 电热鼓风干燥箱：101A-E1，上海实验仪器厂有限公司。 定时恒温磁力搅拌器：JB-3，上海雷磁新泾仪器有限公司。 集热式恒温加热磁力搅拌器：DF-101S，郑州杜甫仪器厂。 量筒、烧杯、胶头滴管、容量瓶、移液管 2.2 PS/CCTO复合材料的制备及性能研究 2.2.1 主要实验原料 苯乙烯：成都市科龙化工试剂厂 偶氮二异丁腈：化学纯，上海山浦化工有限公司 四氢呋喃：分析纯 CCTO：上述所制 苯乙烯在室温下就能缓慢自聚，所以在储存时要加入对苯二酚或叔丁基邻苯二酚2.2.3 主要分析测试方法与测试仪器 ： 扫描电子显微镜：将