从化学反应角度分析,感光高分子材料类型.docVIP

从化学反应角度分析，感光高分子材料类型 摘要：感光高分子材料树脂，他是指高分子体系吸收光能后，在分子间或分子内产生化学反应，吸收光能的不一定指高分子本身，它包括光敏剂等一系列的感光化合物，他们吸收了光能后引起各种的反应，造成聚合物在某种溶剂中溶解度的变化，感光树脂主要用于印刷和集成电路的制作等，光敏高分子材料包括感光树脂，光质变色高分子，光导高分子，高分子光敏剂和增感剂等。 关键词：感光高分子 吸收光能 光敏剂 感光树脂 光质变色高分子 光导高分子 增感剂 English Abstract：Photosensitive polymer material resin, he refers to the polymer system absorb the light, in the molecular or intramolecular produce chemical reaction, absorb the light isnt necessarily refers to the polymer itself, it includes photosensitizer and so on a series of sensitive compounds, they absorb the light energy caused by all kinds of reaction, cause polymer in a solvent solubility change, photosensitive resin is mainly used for printing and integrated circuit production, etc., photosensitive polymer materials including photosensitive resin, light, photo-chromic polymer, optical polymer, polymer photosensitizer and sensitizing agent, etc. Keyword：photosensitive resin Absorb the light photosensitize photosensitive resin Light quality color polymer Optical polymer sensitizer 1感光树脂 1.1 光照后交联或不容交联树脂 溶剂显影后，未曝光的感光树脂溶解，曝光的部分不溶解而形成负像，这种的成为负性树脂。以光交联反应的光致刻食剂有五种。一般光交联剂吸收光能后激发，与聚合物反应，形成交联，例如天然橡胶或聚异戊二烯橡胶进行适度的环化，得到环化橡胶，然后与一种化合物混合，得到光敏刻蚀剂后，因为溶解性好，其分辨率可达到2到3微米，二是因为交联剂的感光性不强，必须加入光敏剂S。后者吸收光能性好将光能转化成光交联剂，它激发后，进行光交联反应，如醇溶性聚酰胺，多官能团单体和光敏剂，如二苯甲酮组成的化合物，三是感光基团键连在高分子主链上，在光的作用下，它被激发，与其他官能团或官能团建和而发生交联反应，例如将苯基马来酰胺亚胺键连在聚甲基丙烯酸酯的主链上，四是由于键连高分子主链上的感光性能不强，需要加入光敏剂，以增强它的感光度。五是聚合物中的官能团，通过光敏剂的作用而进行反应。光聚合是指化合物由于吸收光能而引发化学反应，导致分子链长增加或者产物分子量增加的过程。包括高分子材料的光交联、嵌段共聚和接枝共聚过程。与光交联型感光高分子一样，光聚合过程需要吸收光能产生引发聚合反应的自由基，因此在光聚合型感光高分子材料中需要有光敏结构或者光敏剂、引发剂和增感剂。与光交联型感光高分子材料相区别的地方，光聚合型感光高分子通常以可溶性低聚物或单体化合物为主体。主要作为正性光致抗蚀剂、光敏涂料使用。特别适合于制备印刷用凸版。[1]：（1）有好的感度和好的分辨率，一般的讲，光照射变化的量小，而光的聚合物有很大的溶解度变化。（2）有很好的成膜能力。既形成的模越薄，均匀度越好。（3)薄膜的物理化学性能好。 图1.所需材料的简单单体的结构式 2感光化合物与高分子组成的体系 这类感光高分子是将感光化合物与高分子混合而成的，感光化合物一般为重铬酸钾盐类，芳香族重氮化合物，芳香族叠氮化合物和有机露宿化合物。 2.1重铬酸盐类感光高分子 重铬酸盐类感光高分子是将感光重铬酸盐，通常为重铬酸铵与各种水溶性高分子配置而成，例如将N=500，皂化度为80%—90%的聚乙烯醇90克，在80度下搅拌溶于1000毫升的水中冷却后，加15克重铬酸按既成感光液，将它涂在锌或