TA加氢精制PdC催化剂的制备与表征.pdfVIP

化学通报 2003 年 第66 卷 w084 TA 加氢精制Pd/C 催化剂的制备与表征 畅延青 陈大伟 吴 征 许红兵 穆宇飞 钱 斌 (中石化上海石油化工股份有限公司科技开发公司 上海 200540) 摘 要 通过独具特色的催化剂制备工艺开发了CTP 钯炭催化剂 并使用N -吸附 XRD XRF 2 EPMA 等多种测试手段对催化剂进行了物性表征和活性评价 结果表明 钯炭催化剂的孔径分布状 况和孔型结构及催化剂的制备工艺 都对活性组分钯在载体上的分散分布性能有重要影响 CTP 钯 炭催化剂各项物化性能达到了进口对比催化剂的水平 尤其在落粉和磨耗方面更优于对比催化剂 关键词 对苯二甲酸 钯炭催化剂 加氢精制 PTA Preparation and Characterization of Pd/C Catalysts for TA Hydrogenation Refining Process Chang Yanqing, Chen Dawei, Wu Zheng, Xu Hongbing, Mu Yufei, Qian Bin (Science and Technology Development Company of Shanghai Petrochemical Co., SINOPEC, Shanghai 200540) Abstract CTP Pd/C catalysts were developed through special preparation process, and their physical properties and the catalytic activity were characterized by N -adsorption , XRF, XRD and EPMA techniques. 2 The result indicated that the pore size distribution , micropore structure and preparation process of the catalysts have highly effect on the dispersion and distribution of the palladium on the carbon .The specifications of CTP catalysts could be matched with import catalyst ,especially in abrasion loss and fines content. Key words Terephthalic acid, Pd/C catalyst, Hydrogenation Refining, PTA 工业上通过对二甲苯氧化和粗对苯二甲酸加氢精制两步反应生产精对苯二甲酸 其中加氢 精制过程是在 Pd/C 催化剂作用下 将粗对苯二甲酸中含量为 0.2% 0.4% 的对羧基苯甲醛还原 成易溶于水的对甲基苯甲酸 同时也将粗对苯二甲酸溶液中的微量有色杂质(酮芴 苯偶酰及蒽 醌类等前驱体)进行脱色 最后得到对羧基苯甲醛含量小于25ppm 的纤维级对甲基苯甲酸 [1,2] [3] 对苯二甲酸加氢精制 Pd/C 催化剂的专利报道已有几