电炉含锌粉尘在微波场下脱锌的试验研究.PDFVIP

Series No. 356 金 属 矿 山 总第356 期 February 2006 METAL MINE 2006年第2 期 电炉含锌粉尘在微波场下脱锌的试验研究* 周 云 彭开玉 李辽沙 王世俊 王海川 董元篪 （安徽工业大学） 摘 要 微波能是一种清洁型能源，可以对物料进行选择性体加热。利用电炉含锌粉尘和煤粉吸收微波能力 强的特点，试验研究了微波加热还原电炉含锌粉尘的脱锌效果。结果表明，在大气条件下，脱锌率可达到80% 左 右；脱锌率随着配煤量、煤粉粒度和微波功率的增加而提高。 关键词 电炉含锌粉尘 微波 脱锌率 Experimental Research of Zinc Removal from Dust of EAF in Microwave Field Zhou Yun Peng Kaiyu Li Liaosha Wang Shijun Wang Haichuan Dong Yuanchi （Anhui University of Technology ） Abstract Microwave is a kind of clean energy and can heat the material selectively. By taking advantage of the char- acteristics of strong ability to absorb microwave of zinc-borne dust of EAF and coal powder，experimental research was made of the effect of zinc removal from zinc-borne dust of EAF by microwave heating. The results show that ，under the atmos- phere condition ，the zinc removal rate can reach about 80% and will increase with the increase of the coal ratio ，the parti- cle size of coal powder and the microwave power. Keywords Zinc-borne dust of EAF ，Microwave ，Zinc removal rate 钢铁厂每年要产出大量的含铁尘泥（如高炉瓦 艺。因锌的沸点很低（约900 ℃ ），所以如果对微波 斯泥、转炉OG 泥、电炉粉尘等），其铁含量较高（约 炉进行改装，增加烟气回收系统，可以回收锌；另外， 50% ），是一种很有价值的二次资源，但有一部分因 脱锌后的粉尘若锌含量能降至很低，可被送往烧结 锌含量过高，使其不能在钢铁厂内部回收利用，如送 厂烧结，从而实现尘泥中锌和铁的回收利用。本试 往炼锌厂，又因锌品位太低而提高冶炼成本。目前 验以电炉含锌粉尘为原料，初步探讨了其在微波场 处理钢铁厂含锌尘泥的工艺主要有3 种：物理法、湿 下脱锌的基本规律。 法和火法。物理法效率较低，一般作为湿法和火法 1 试验装置和方法 的预处理工艺；湿法工艺主要用来富集尘泥中的锌， 微波加热设备采用可调式箱式工业加热微波 富集率虽然很高，但处理后的渣滓中锌含量仍然超 炉，微波加热频率为2 . 45 GHz ，功率输出范围为0 ～ 标，而使尘泥中的铁无法