# 攀钢 3 转炉大流量氧枪试验研究 1 1 1 2 2 1 陈 均 梁新腾 曾建华 杨森祥 刘荣蒂 （1．攀钢集团研究院有限公司，成都 611731 ；2 ．攀钢钒提钒炼钢厂，攀枝花 617062 ） 摘 要 攀钢钒炼钢厂为改善氧枪使用效果对新设计的5 孔氧枪喷头进行生产试验。试验结果表明，随着供氧压力 的增大，氧气流量不断增大，在相同的工作压力下新设计的喷头具有更好的冶金效果：供氧流量平均增加了932h/m3 ， 初渣形成时间平均提前1.33min，纯吹氧时间平均缩短0.84min，脱磷效果及热效率更好。 关键词 转炉 氧枪 喷头 供氧强度 Study on Large Volume Oxygen Lance for 3# Converter in Pangang Group Chen Jun1 Liang Xinteng1 Zeng Jianhua1 Yang Senxiang2 Liu Rongdi2 （1. Pangang Group Research Institute Co., Ltd., Chengdu, 611731; 2. Vanadium-recovering and Steel-making Plant of PZH Steel, Panzhihua, 617062 ） Abstract To improve the effect of the oxygen nozzle, a new 536 nozzle is designed and industrial tests are carried out. The results indicate that the oxygen flow increased with the improving of oxygen supply strength and at the same working 3 pressure, the new designed nozzle has a better metallurgical effect, the average oxygen flow is increased by 932 h/m , the average slag-forming time and blowing time are shortened by 1.33min and 0.77min respectively, and a better dephosphorization effect and thermal efficiency are obtained by the new nozzle. Key words converter, oxygen lance, nozzle, oxygen supply strength 1 引言 攀钢钒老转炉冶炼周期比新转炉要长7～9min，设备维护时间较为紧张，随着铁水产量的进一步提高以 及3 号方（圆）坯正式投产使转炉的冶炼任务加重，为了更好地满足生产的要求，迫切需要开展老转炉高效 供氧技术研究，以提高老转炉供氧强度，降低吹炼时间。为此，攀钢钒提钒炼钢厂针对老区炉型特点和冶炼 工艺情况对氧枪喷头进行了优化设计，并通过工业试验对新喷头的冶金效果进行了考察。 2 喷头优化 针对攀钢3 号炉现役的喷头冶炼时易出现返干、喷溅及粘枪的情况，新设计的喷头对喷孔夹角、喉口直 径、出口直径等参数都进行了相应的优化，具体参数见表1。 陈均，男，本科，工程师，从事炼钢工艺研究，foresttiger119@163.com 8-30 第八