冷酸轧激光焊机生产高强钢工艺的研究 黄秋菊 于 宁 （鞍钢股份有限公司，鞍山 114003） 摘 要 通过不同的米巴赫激光焊机的不同生产工艺进行生产高强钢冷轧钢带的对比研究，得出生产冷轧高强钢最 适宜的生产工艺。试验证明具有预热系统的激光焊机选择合理的工艺焊接的焊缝具有很好的韧性，轧机断带率很低。 关键词 米巴赫焊机 高强钢 工艺 TheStudyonHighStrengthSteelProcessof MiebachWeldingMachineinPicklingLine Huang Qiuju Yu Ning (Angang Steel Company Limited, Anshan, 114003) Abstract The perfect process of welding high strength cold rolling was received by studying on different pilot productions at Miebach laser Welder. The test approved the laser welder with preheater easily choice retional welding schedule for good welded joint, then welding seam has good toughness so that ratio of strip breakage will be very low. Key words miebach welding machine, high strength steel, process 1 引言 冷轧酸轧机组激光焊机焊接热轧钢带具有对接焊缝牢固，轧制中动态厚度超差长度较短，轧机断带风险 低等优势，使得激光焊机成为冷轧生产钢带的优选设备。但是对于激光焊机焊接高强钢带仍然存在着焊接焊 缝淬硬性和冷裂及脆化的问题。 根据化学成分对钢材焊接焊缝区淬硬性的影响程度，粗略评价焊接时产生冷裂及脆化倾向的计算方法。 Cep=C+Mn/6+(Cr+Mo+V)/5+(Ni+Cu)/15[1] Cep0.4%焊接性优良。当0.4%Cep0.6% 时，钢材淬硬倾向明显，可焊接性下降，冷轧高强产品的平均Cep 均大于0.4% 。 对于高强钢焊缝区冷裂纹敏感性，用焊接裂纹敏感措施Pcm 确定。钢的Pcm 值越低，焊缝区冷裂纹敏 感性越低。 Pcm( ％)=C+Si/30+(Cu+Cr+Mn)/20+Ni/60−I−Mo/15+V/10−t−5B[1] 所以冷轧酸轧机组生产高强钢带具有很大的困难，经常会因为热轧钢带的碳当量较高，焊接焊缝不良造 成冷轧轧机断带，影响生产的顺利进行和延误生产节奏。选择正确的激光焊接工艺具有很重要的意义。 2 激光焊机的特征 激光焊机主要分为：谐振器（内含激光源）2 个、光传输通道、剪切机、夹紧装置、导向器、碾压辊、 气动系统、冲孔、挖边剪。前后伴有预热装置( 图1)。 8-168 第八届（2011 ）中国钢铁年会论文集 激 光 枪 夹板器 图1 焊机焊接主部件图 （1）工艺过程：夹紧装置对接剪切后断面，对接后激光束从操作侧向传动侧进行激光加热，碾压辊在 其后碾压平整焊缝。 （2 ）焊缝特点：属于熔融焊，有相变反应，焊缝区窄0.4mm，对接焊缝牢固，轧制中需要焊缝过焊机 时抬焊缝，动态厚度超差长度很较短可达15 米范围，轧机断带风险低，高碳高强钢焊缝发生相变易产生魏 氏体，脆化组织，轧制易发生断带。 （3 ）加前后预热装置的激光焊机：针对焊缝温