一种质量特异炼焦煤的实验与研究.pdfVIP

一种质量特异炼焦煤的实验与研究 刘克辉 钟树周 叶远欢 梁开慧 (广东省韶关钢铁集团有限公司，韶关 512123) 摘 要 采用煤岩分析和基氏流动度检测方法、结合灰成分及其矿物质催化指数分析、单种煤炼焦、配煤炼焦及其 焦炭热强度实验等手段，发现一种质量特异的韶钢炼焦煤并进行研究，指出仅凭 G、Y 值和工业分析指标不能准确 判断炼焦煤煤质，需要灵活运用相关指标和实验分析手段综合判断，从而发掘性价比高的炼焦煤资源或避免生产过 程中的质量风险。 关键词 炼焦煤 质量 实验 研究 Experiments and Studies on the Coking Coal of Specific Performance Liu Kehui Zhong Shuzhou Ye Yuanhuan Liang Kaihui (CSG, Shaoguan, 512123) Abstract The coking coal of specific performance was found at CSG through petrographic analysis, measuring the Giseller fluidity, analyzing ash composition and catalytic indices of its mineral substances, coking by a single kind of coal and by blended coal and heat intensity experiments. Studies were made on the coking coal. Thus the performance of coking coal could not be determined accurately only by G and Y values and industrial indices, it should be determined by flexibly utilizing the indices concerned and experiments so as to find coking coal of good performance at low cost and avoid accident risks during production. Key words coking coal, performance, experiments, studies 1 引言 在韶钢主要单种煤结焦性能研究项目实施过程中，发现某船进口炼焦煤（以下简称 A 焦煤）煤质特异。 其常规的煤质指标 G 值、Y 值、工业分析指标等与其他同类焦煤相近，甚至优于其他同类焦煤，但采用煤岩 分析和基氏流动度检测方法分析，发现其显微组分异常，活惰比高达 19.26，最大流动度仅32 DDPM，通过 单种煤炼焦实验、配煤炼焦实验等方法进一步检测分析，发现其热强度相比其他同类焦煤显著偏低，配煤实 验显示随着替代同类焦煤的配入量增加，焦炭热强度下降，配入（替代）量越大时，下降越明显（尽管热强 度不能准确反映焦炭在高炉内的热态性能，但目前仍是重要的质量判断指标）。 2 实验方法 采用意大利 PL2000 型流动度检测仪，依据 ASTM 标准 D2639 ，对煤样进行全自动检测，分析其开始软 化温度、最大流动度、最大流动度温度、固化温度、塑性区间等指标。 采用蔡司显微镜，HD 型煤岩及焦炭显微结构分析仪，依据 GB6948—2008 ；在反光显微镜下用油浸物 镜人工测定煤光片中镜质组最大反射率、随机反射率发布、煤岩显微组分。 8-268 第八届（2011 ）中国钢