攀钢型煤炼焦技术研究 1 2 11 黄先佑 祝永强 舒文东 （1.攀钢集团研究院有限公司；2.攀钢集团攀枝花钢钒有限公司煤化工厂） 摘 要 在炼焦煤资源日益紧张，焦炭质量与优质炼焦煤资源之间的矛盾日趋突出的背景下，攀钢为了提高焦炭质 量、扩大炼焦煤源而开展了配型煤炼焦试验，通过配型煤小焦炉试验表明：配型煤炼焦的型煤适合配比为 30%。通 过小焦炉试验和工业试验表明：配型煤炼焦可使焦炭质量得到明显的改善，焦炭的 M40 可提高 0.6～7.2 个百分点， M10 可改善 1.1～3.8 个百分点，焦炭反应后强度提高 2.15～6.82 个百分点。 关键词 型煤 炼焦 焦炭质量 Research on Cokemaking Technology by Coal Briquetting of Pangang Huang Xianyou1 Zhu Yongqiang2 Shu Wendong1 （1.Pangang Group Research Institute Co., Ltd., Panzhihua, 617000; 2. Pangang Group Panzhihua Steel ＆ Vanadium Co.,Ltd.,Panzhihua, 617022 ） Abstract In the background that the shortage of coking coal resources was increasing serious and the contradiction between coke quality and high quality coking coal resources was increasingly prominent, in order to improve PanGang’s coke quality and expand coking coal resources, coking tests by coal briquetting were carried out. The results of small coke oven experiments showed that the suitable ratio of heart patient coal was 30%. The results of small coke oven experiments and industrial experiments indicated that coal briquetting process could improve coke quality evidently, coke’s M40 could increase 0.6 ～ 7.2 percentage points, M10 decrease 1.1 ～ 3.8 percentage point and CSR increase 2.15 ～ 6.82 percentage points. Key words coal briquetting, cokemaking, coke quality 1 引言 随着焦化的快速发展，炼焦煤的消耗量急剧增加，炼焦煤价格不断上涨，炼焦成本不断上升，使得优质 炼焦煤资源与焦炭质量之间的矛盾日益突出。为了缓解这种矛盾和提高焦炭质量，攀钢进行了配型煤炼焦试 验研究。配型煤炼焦是将一部分装炉煤在装入焦炉前配入黏结剂加压成型块，然后与散状装炉煤按比例混合 后装炉的一种炼焦煤准备的特殊技术措施。配型煤有扩大炼焦煤源、增加劣质炼焦煤配用量的作用。通过小 焦炉试验研究和工业试验研究表明：配型煤炼焦可使焦炭质量得到明显的改善，M40 可提高 0.6～7.2 个百分 点，M10 可改善 1.1～3.8 个百分点，焦炭反应后强度（CSR ）提高2.15～6.82 个百分点。