轧制工艺对钢板内部质量影响的研究 张苏渊 朱振华 李春智 （首钢技术研究院，北京 100043 ） 摘 要 随着高级钢种的研究开发，内部质量对钢板综合质量影响更加显著；获得和改善钢板内部质量的工作已经 受到广大科技人员的越来越多的关注。钢材内部质量主要取决于冶炼连铸生产过程，轧制过程也具有一定的改善作 用。本文立足于理论分析，通过试验室实验和实际例子等计算来阐述轧制力、压下量、轧制速度等对改善钢板内部 质量的作用，并以实例做说明。 关键词 轧制力 轧制速度 压下量 Study on the Improvement of the Rolling Process to Plate’s Inner Quality Zhang Suyuan Zhu Zhenhua Li Chunzhi （Shougang Research Institute of Technology, Beijing, 100043） Abstract With more studies on the new higher grade steels, the inner quality has been one of the most important facts to plates’ combination property. More and more studies have been taken to get how to improve the inner quality. In the processes, melting, continue casting and rolling are the mayor ones. As we know, melting and continue casting can reduce the inner defects such as crack, inclusion and rarefaction which exist in the slabs. During controlling the rolling process parameters, plates’ inner quality can be improved, including rolling velocity, depression and so on. Base on theories, tests and calculating, this article will show how the rolling power, depression and rolling velocity to improve the plate’s quality. Some examples will explain it more visually. Key words rolling force, rolling velocity, depression 1 引言 随着高等级钢种比率的升高，钢板内部质量也受到越来越大的重视。钢板的内部质量主要决定于连铸坯 质量。一般，炼钢部门通过采取相应的措施来减少内部缺陷包括裂纹、夹杂物、偏析、疏松等。轧钢部门则 是通过适当地调整生产工艺来尽量减缓或改善内部缺陷对钢板质量的影响。 目前，国内关于通过改善轧制生产工艺来减轻钢板内部缺陷的研究较少，本文主要采用理论计算和分析 的方法，比较粗浅地讨论调整轧制工艺来减缓或压合心部裂纹，从而起到改善钢板内部质量的作用。 2 变形区形状系数对钢板内部变形的关系 钢板轧制是一种不均匀变形，其厚度上变形分布与变形区形状系数( ｌ/ h )有关。理论上，随着 ｌ/ h 值 越大，变形进入钢板内部越深。当 ｌ/ h 0.5~1.0 （轧制厚件）时，钢板表面层变形较中心层要大；当ｌ 8-440 第八届（2011 ）中国钢铁年会论文集 / h