热轧板坯加热工艺优化.pdfVIP

热轧板坯加热工艺优化 1 2 刘 勇 李俊洪 （1.攀钢集团攀枝花钢钒有限公司热轧板厂, 攀枝花 617000 ；2. 攀枝花钢铁研究院, 攀枝花 617062 ） 摘 要 建立了三段步进梁式加热炉板坯加热过程数学模型，用全隐式有限差分法对数学模型进行离散化，开发了 板坯温度场计算模型。采用该模型重点研究了板坯宽度对板坯中心温度变化过程的影响规律。研究结果表明，对于 厚度为 200mm 的板坯，当板坯宽度大于600mm 时，板坯中心温度变化过程与板坯宽度无关。以此为根据，优化了 板坯加热工艺，达到了提高生产效率并节能减排的目的。 关键词 步进梁式加热炉 板坯加热 温度场 优化 Optimization of Slab’s Reheating Process Liu Yong1 Li Junhong2 (1. Pangang Group Panzhihua Steel ＆ Vanadium Co.,Ltd., Panzhihua, 617000; 2. Panzhihua Iron Steel Research Institute, Panzhihua, 617062) Abstract A mathematical model for slabs heated in a 3-zone walking beam type of re-heating furnace was established．The finite difference method was used for discretion of the mathematical model and a computational software was developed ．The influence of the slab’s width on the change regularity of the slab’s temperature was studied. It was founded that, to the 200mm-thick slab, when the width was above 600mm, the slab’s width has no influence on the slab’s center point temperature. According to the result, the slab’s reheating process was optimized, which improved the productivity and saved the energy. Key words walking beam heating furnace, slab reheating, temperature field, optimize 板坯加热过程是一个复杂的物理化学过程，受板坯尺寸、装炉温度、热物性参数以及加热炉尺寸、燃料 种类、加热能力等多种因素影响。研究有关因素对板坯加热过程的影响规律及影响程度,可优化加热工艺从 而达到提高加热效率和降低能耗的目的。 近年来，人们[1,2,3]对热轧板坯加热温度变化过程进行了许多研究，对提高加热效率、降低板坯氧化烧损 起到了积极作用。本文建立了攀钢 1450 热轧三段步进梁式加热炉板坯加热过程数学模型，采用全隐式有限 差分法对模型进行离散，在 FORTRAN POWERSTATION 软件平台开发了板坯加热过程温度场计算程序。 以该程序为基础，模拟了 1450mm 热轧板坯加热过程温度变化过程，重点研究板坯宽度对板坯中心温度变 化过程的影响规律。以此为根据，优化了 1450 热轧板坯加热工艺，达到了提高生产效率并节能减排的目的。 1 板坯加热过程热传导数学模型 1.1 热传导微分方程 1450 热轧步进梁式加热炉结构如图 1 所示。鉴于加热炉中板坯加热过程的复杂