1结合热轧机组特点合理使用支撑辊 史志勇 荆 涛 董宝权 于 浩 （本溪钢铁（集团）公司热轧厂，本溪 117000 ） 摘 要 简述机组的不同特点及所承担的主要品种规格，分析了支持辊在使用过程中出现的问题，并根据生产实际 对支持辊辊型设计、换辊制度、磨削制度进行了相关的工艺参数及工艺制度的优化和改进，最大限度地发挥了支持 辊的价值。 关键词 热轧机组 产品结构 支撑辊 辊型设计 轧辊磨损 导角 换辊制度 Application Optimization of BUR According to the Mill Features Shi Zhiyong Jing Tao Dong Baoquan Yu Hao （Hot Strip Mill of BX Iron ＆ Steel Co., Ltd., Benxi, 117000 ） Abstract This paper mainly analysed the problems which happened during the application of Buckup roll on different rolling mill which focus on different varieties and size of steel grades, and optimize and improve technical data as well as the rolling strtegies related to Buckup roll profile, BUR changing system, grinding system etc. According to the production realities so that BUR’s value could be realized as much as possible. Key words hot rolling mill, products structure, buckup roll, roll profile design, roll wear, edge relief, roll changing system 1 引言 本溪钢铁（集团）公司热轧厂共管辖 3 条热轧机组，分别为 1700mm 热轧宽带钢轧机、1880mm 薄板坯 连铸连轧机及 2300mm 热轧宽带钢轧机。三套热轧机组各有特点，为了有效地发挥每套轧机的优势，各机 组在产品品种规格上有大致分工，具体如下。 1.1 1700mm 常规热轧带钢轧机 产能 350 万吨，1700mm 常规热轧带钢轧机工艺流程如图 1 所示。 1700mm 机组主要承担的品种结构如下： （1）以宽度规格在 1350mm 以下普通冲压级汽车内板、家电用深冲级及普通结构用冷轧原料卷 为主。 （2 ）生产部分优质碳素钢、结构钢、汽车结构钢等热轧产品。 史志勇（1976—），男，轧钢工程师，ashi7608@163.com 结合热轧机组特点合理使用支撑辊 8-241 图 1 1700mm 热轧机工艺流程 1.2 1880mm 薄板坯连铸连轧线 本钢薄板坯连铸连轧生产线主要由 1 座 LF 钢包精炼炉和 1 台 RH 真空炉、两台意大利达涅利公司 (DANIELI) 的薄板坯连铸机、两条美国布里克蒙公司(BRICMONT) 的辊底式加热炉、日本三菱日立公司 (MITSUBISHI-HITACHI)的两架粗轧机、一套中间冷却装置、5 架精轧机、1 条层流冷却线以及两台地下卷 取机组成，设计产能 280 万吨。本钢薄板坯连铸连轧生产线装备和工艺流程如图 2 所示。 图2 本钢 1880mm 热轧机工艺流程 1880 机组主要承担的品种结构如下： （1）轧线采用半无头轧制技术及装备