热轧双相钢检验结果分析与对策.pdfVIP

1热轧双相钢检验结果分析与对策 张立龙 （本钢技术中心, 本溪 117000 ） 摘 要 简要说明了热轧双相钢组织及生产特点, 并结合本钢热轧双相钢的试验生产，分析了双相钢强度高、伸长 率低的原因，介绍了工艺条件对 C-Si-Mn-Nb 系双相钢组织性能的影响，为下一步工艺参数的确定提供了参考。综 合分析不同类型原因导致强度高的情况后提出了对于降低双相钢强度、稳定生产的建议。 关键词 热轧双相钢 工艺参数 抗拉强度 Hot-rolled Duplex Steel Inspection Results Analysis and Countermeasures Zhang Lilong ( Benxi Iron Steel(Group) Co., Ltd, Benxi, 117000 ) Abstract Briefly explain the hot-rolled duplex steel organizations and production, and combining the characteristics of benxi steel hot-rolled duplex steel production, analyzes the test duplex steel strength GaoYanShen rate low reason, introduces technological conditions of C - Si - Mn - Nb duplex steel organization performance of the influence of process parameters for the next step, the sure are provided. Comprehensive analysis of different types cause of the high strength forward for reducing after duplex steel strength, stable production suggestion. Key words hot-rolled duplex steel, process parameters, tensile strength 通过热轧控轧控冷工艺，采用合适的化学成分, 控制带钢终轧温度、冷却速度及卷取温度获得铁素体＋ 马氏体双相组织,这种双相钢称为热轧双相钢。 近年来, 随着汽车向节能、减重和安全性方向发展, 热轧双相钢以其高强度和高成形性能, 已广泛地用 于制造汽车加强板、车轮、底盘、保险杠、车体各种框架等构件。可减轻重量 20%～30 ％，符合汽车材料 轻量化、高性能、安全环保节能的发展主题，逐渐成为汽车用钢的首选钢种之一。 本钢采用低温卷取型控轧工艺，对热轧双相钢进行了实验生产。其原理是在终轧后，马上进行冷却，避 开两相区铁素体先析出的区间，冷却到 Ar 1 温度以下后，空冷一段时间完成大部分的 A→F 相变,而在此后 的快冷阶段迅速将钢带冷却至Ms 点以下卷取,得到 F+M 组织。卷取温度低于 300℃，避免贝氏体组织形成， 同时也避免了铁素体的时效和马氏体的自回火。低温卷取的冷却工艺图见图 1。 张立龙（1982-），男，毕业于东北大学材料物理专业，本钢技术中心高强所研发员，邮箱、 联系电话：0414-7827241 。 8-190 第八届（2011 ）中国钢铁年会论文集 图 1 低温卷取冷却工艺图 1 实验材料与方法 1.1 实验材料 试验生产的热轧双相钢的成分