热轧石油套管 N80-1 性能研究 逯登尧 刘发友 1 （山东寿光巨能特钢有限公司，寿光 262711 ） 摘 要 N80-1 石油套管用热轧管的屈服强度，主要受定径后钢管的冷却速度影响，在Ar3 至Ar1 的温度区间采用 风冷可有效抑制钢中的奥氏体向铁素体转变，从而显著提高其强度；控制钢中碳含量，适当增加钒和锰的含量，也 有助于钢管强度的提高；过高的加热温度和过长的加热时间会导致成品钢管的晶粒过分长大，而使钢管的韧性变坏。 关键词 热轧 石油套管 N80-1 拉伸性能 冲击性能 Hot-rolled Oil Casing Pipe N80-1 Performance Research Lu Dengyao Liu Fayou (Shandong Shouguang Juneng Special Steel Co., Ltd., Shouguang, 262711) Abstract N80-1 oil casing pipe with the hot rolling pipe yield strength, mainly affected by sizing the cooling speed after the impact of steel in the temperature range of Ar3 to Ar1 can effectively inhibit the use of air-cooled steel in the austenite to ferrite transformation, which significantly improve their strength; control of carbon content, and appropriately increase the content of vanadium and manganese, but also help increase the strength of steel; high heating temperature and heating time is too long will lead to excessive grain growth of steel products, and deterioration of the toughness of steel. Key words hot-rolled, oil casing pipe, N80-1,stretch performance, impact performance 1 引言 非热处理钢是指钢热加工后不进行重结晶热处理而使用者或只进行回火使用者。传统的非热处理钢为建 筑用的低碳钢和低碳低合金钢，以及现代控轧、控冷技术进步而形成的低碳微合金化高强度低合金钢与中碳 ［］ 微合金化非调质钢，高性能的非热处理钢的核心是采用控轧控冷 1 。用36Mn2V 生产的石油用套管N80-1 就属于后者。 N80-1 为API 5CT 标准中的一个钢级，它可采用热轧后正火或控制轧制方式交货，其化学成分除了对P 、 S 的要求外，其他成分未做任何规定，国内目前均采用36Mn2V 这个牌号来生产N80-1 。为了节约制造成本， 除将36Mn2V 中V 的含量控制在0.11%～0.16%外，为保证钢管的力学性能，主要依靠控轧控冷来实现对钢 中铁素体机体的强化。由于热轧成品钢管的终轧温度波动范围比较大，为稳定定径前的温度，一般采用再加 热方式来控制定径前温度，从而获得稳定的成品钢管机械性能。再加热过程主要关注钢管的加热温度和保温 时间，其次是成品钢管的冷却速度，它们决定着钢管的最终性能。本文主要探讨再加热和轧后冷却工艺对成 品钢管力学性能的影响。 2 工艺流程 80 tBOF→70 tLF→R12 m CCM （五机五流）→φ180