卷取温度对热轧TRIP钢力学性能的影响.pdfVIP

卷取温度对热轧 TRIP 钢力学性能的影响 高绪涛 赵爱民 赵征志 靖海涛 杨顺利 单元胜 （北京科技大学冶金工程研究院，北京 100083 ） 1 摘 要 为了研究卷取温度对热轧TRIP 钢力学性能的影响，使用金相显微镜、X 射线衍射、拉伸实验等方法对三 种卷取温度下制备的热轧TRIP 钢进行分析。结果显示，随着卷取温度降低，残奥体积分数和碳含量变少。热轧TRIP 钢的力学性能随着卷取温度的降低，表现为高的屈服强度和低延伸率，450 ℃卷取温度下制备的热轧 TRIP 钢的综 合力学性能最优。 关键词 热轧TRIP 钢 卷取温度 残奥碳含量 残奥体积分数 Effect of Coiling Temperature on Mechanical Properties in Hot Rolled TRIP Steel Gao Xutao Zhao Aimin Zhao Zhengzhi Jing Haitao Yang Shunli Shan Yuansheng (Metallurgical Engineering Research Institute, University of Science and Technology Beijing, Beijing, 100083) Abstract For studying the effect mechanical properties of hot rolled transformation -induced plasticity (TRIP) steels which are prepared through three different coiling temperature,optical microscopy(OM), X-ray diffraction(XRD),and tensile test are used.The results show that amount,carbon content of retained austenite of the testing steel get less with lower coiling temperature. When the coiling temperature become lower,yield strength is higher, elongation becomes lower.Comprehensive mechanical properties of the testing steel which is coiled at 450 ℃ is the best. Key words hot rolled TRIP steels, coiling temperature, carbon content of retained austenite, volume fraction of retained austenite 1 引言 经合理的轧后冷却工艺，可使低合金钢在室温下含有一定量的残余奥氏体，这部分残余奥氏体在应力作 用下发生马氏体相变，产生TRIP ( Transformation-Induced Plasticity)效应，能同时得到良好的延展性和高强 度的特点[1～3] 。TRIP 钢板用作汽车构件可减轻车重，降低油耗，抵御撞击时的塑性变形能力强，保障了驾乘 人员的安全，具有明显的优越性，应用前景广阔。 2 试样制备与试验方法 实验钢采用50Kg 真空中频感应炉冶炼，化学成分（质量分数，% ）为：C 0.10~0.20，Si 1.0~2.0，Mn 1.0~2.0 ， Nb0.01~0.08 ，V0.05~0.1 余量为铁。将铸锭锻造并加工成规格为40mm×80 mm×90 mm 的锻坯。将锻坯经六 道次热轧成厚度为4mm 的薄板，钢坯加热温度、开轧温度和终轧温度分别为1200℃、1150℃和850℃。终 轧后分别以3 种不同卷取制备热轧TRIP 钢。1 号、2 号和3 号试验钢终轧后水冷至750℃，随后继续空冷至 高绪涛（1976-），男，博士研究生，从事汽车用钢研究，xut