鞍钢2150ASP转炉低氮钢生产工艺开发.pdfVIP

鞍钢 2150ASP 转炉低氮钢生产工艺开发 简 龙 温铁光 王 鹏 王文科 （鞍钢股份炼钢总厂） 1 摘 要 本文根据鞍钢 2150 生产线生产的低氮钢种，利用统计的方法得出钢中氮含量随转炉冶炼终点钢中碳含量 的增加、渣量的增加、补吹时间的缩短和脱氧程度的减弱而降低；而与转炉出钢过程时间的长短和是否采用底吹工 艺相关性不强的结论，有利于现场指导低氮钢的生产。 关键词 低氮钢 脱氮 转炉冶炼 The BOF Steelmaking Process of LN Steel at 2150ASP in Ansteel Jian Long Wen Tieguang Wang Peng Wang Wenke （No.3 Steelmaking and Rolling Plant of Ansteel ） Abstract According to the ULN steel grade produced at 2150 ASP in Ansteel, adopted the Stat. method, it could be found that the content of N in steel at the end of blowing increase along with carbon and silicon in hot metal increase. And the N in steel increase along with the time of re-blowing and degree of deoxidation debase. But the N in steel has nothing to do with the time of tapping and the bottom blowing mode. These conclusions are propitious to instruct the production of ULN steel grade. Key words LN steel, denitridation, converter smelting 1 引言 随着技术的发展，用户对钢的质量要求越来越苛刻，对钢的纯净度要求越来越高。钢中的氮含量对钢材 的性能影响较大，其氮化物（FexN ）的析出，会导致钢材产生时效和蓝脆现象，造成钢材的屈服极限、强度 极限和硬度提高，韧性、塑性、深冲性能、HAZ 性能、热加工性能、导电性能和焊接性能下降，还易造成 铸坯产生开裂和引起晶间腐蚀。另外钢中的氮极易与钢中的钛、铝等元素形成带有棱角的夹杂物，降低钢材 的洁净度，影响其拉拔性能[1~6] 。如果钢中的溶解氮含量超过一定的极限还有可能在铸坯内形成气泡和疏松 缺陷[7] 。因此，除耐热钢及不锈钢外，应当尽可能地降低钢中的氮含量。 鞍钢 2150ASP 生产线作为鞍钢的精品板材生产基地，承接着鞍钢超过一半的冷轧超深冲钢（IF 钢）的 生产合同，此类钢种为了保证在后序深冲过程中具有较高的延展性，对钢中氮含量的要求极为严格。本文研 究的主要内容是针对鞍钢 2150ASP 生产线围绕转炉冶炼工艺，在如何建立稳定的、低成本的纯净钢生产工 艺平台所做的一系列工作之一。 简龙 (1973-) ，男，硕士研究生，工程师，目前从事炼钢工艺技术管理工作, 电话 jlzljn@163.com 鞍钢2150ASP 转炉低氮钢生产工艺开发 8-727 2 研究范围 [8] 针对低氮类钢种，由于钢中氮含量较低，在 RH 工序的处理过程中，难以实现进上步脱氮 。而复吹转 [