鞍钢RH轻处理钢种生产工艺实践.pdfVIP

鞍钢 RH 轻处理钢种生产工艺实践 王鹏飞 张 越 田 勇 毛志勇 王 鹏 温铁光 （鞍钢股份有限公司第三炼钢连轧厂，鞍山 114021 ） 摘 要 本文针对鞍钢第三炼钢连轧厂的实际情况，系统介绍了采用铁水预处理—顶底复吹转炉冶炼—RH 精炼生 产低碳低硅铝镇静钢的工艺实践。其主要特点是RH 真空处理不等过程样、根据过程氧值一次性调整钢中Als ，根 据氩站样一次性调整钢中C、Mn 成分，使真空处理时间控制在20min 以内的比率达到95%，满足真空室在一个浇 次生产7 罐低碳低硅铝镇静钢的需要。1 关键词 低碳低硅铝镇静钢 RH 精炼 轻处理 Process of RH Light Treatment Steel at Ansteel Co., Ltd. Wang Pengfei Zhang Yue Tian Yong Mao Zhiyong Wang Peng Wen Tieguang (No.3 Steelmaking Continuous Rolling Plant, Angang Steel Co., Ltd., Anshan, 114021) Abstract In this paper, a new process which consists of pretreatment of hot metal, combined blown BOF, rimmed steel tapping with slag skimming process, RH-TB vacuum treatment for low carbon and low silicon aluminum killed steel. The process does not need process sample and can one-off adjust C, Mn and Al content in molten steel. Thus the treatment s period was controlled lower than 20min and satisfied requirement of producing seven ladle of molten steel in one casting sequence. Key words low carbon and low silicon Al killed steel, RH refining, light treatment 1 引言 鞍钢第三炼钢连轧厂现有2 座脱硫位，3 座260t 顶底复吹转炉，配备2 座LF 炉、2 座RH 精炼炉，2 台板坯连铸机。目前该厂通过LF 炉精炼的钢种比重大约为70% 以上，造成LF 精炼炉负荷较大，能源和渣 料消耗量都很大。 为了降低LF 炉作业率，释放RH 产能，同时也为在建的新连铸机的投产做好精炼-连铸的生产流程匹配， 必须将一部分原来采用RH-LF 双联法冶炼的低碳低硅钢种和通过LF 炉直上的低硅铝镇静钢通过RH 处理后 直接上机浇注，由于RH 插入管连续使用时间不大于 150min，因此在没有特殊情况的前提下，此类钢种的 处理时间必须控制在20min 以内，以达到一个浇次能够生产7 罐钢的需要[1] 。 2 新旧工艺流程概述 为了避免RH 处理过程大量加入合金，给RH 处理带来困难，在实际生产中限定了经RH 处理后直接上 机浇注的钢种条件，要求[C]≤0.10%、[Mn]≤0.30%，本文选取了3 个钢种进行，具体成分见表1。 王鹏飞，男，学士，工程师，从事炼钢技术管理。 8-220 第八届（2011 ）中国钢铁年会论文集 表 1 RH 轻处理钢种成分列表 钢种 C Si Mn P S Als N AYHS5 0.010～0.030