铝合金无铬磷化处理.pdfVIP

铝合金无铬磷化处理 1 2 张圣麟 ,张小麟 1 河南师范大学 化学与环境科学学院 新乡 453007; 2 河南工业大学 化学化工学院，郑州 450052; 摘要 研制了一种不含铬的低温快速磷化液,研究了游离酸度、温度和所含物质对铝合金磷 化效果的影响;并通过 X 射线衍射及能谱、扫描电镜、电化学等方法研究了磷化膜的晶相、 形貌、耐蚀性.结果表明,该磷化液在 35～45℃,5～8min 时,能在 6061 铝合金上形成一层致密 2 均匀的磷化膜，膜重 4～6g/m ，做油漆的底层具有良好的应用前景. 关键词:铝合金;无铬磷化;锌系 中图分类号:TG174. 4 　　　文献标识码: B 文章编号:1002-6495(2008)04-0279-04 CHROMATE-FREE PHOSPHATING OF ALUMINUM ALLOY ZHANG Sheng-lin 1 ZHANG Xiao-lin2 1.Chemistry Environmental Science College,Henan Normal University, Xinxiang 453007; 2.School of Chemistry and Chemical Engineering,Henan University of Technology,Zhenghou 450052; Abstract: A chromate-free phosphating solution has been developed. The effects of free acidity, temperature and compositions of phosphating solution on phosphating for aluminum alloy have been studied. The crystal phase, morphology and corrosion resistance of phosphate coating have been investigated by scanning electron microscopy (SEM), X-ray diffraction (XRD), energy-dispersive X-ray (EDX) and electrochemical measurements. It has shown that the phosphate coating formed in chromate-free phosphating solution at 35～45℃ for 5～8 min can 2 give a good performance, with a weight about 4～ 6g/m .It can be used for aluminum alloy pretreatment and painting. Key words: Aluminum alloy, Chromate-free phosphating, Zinc base 纯铝的机械强度低，为此常加入镁、锌、铜、硅和锰等元素对其改性，改性后的铝合金 机械强度增加，但耐蚀性有所降低，为此需对铝合金进行表面处理. 目前，铝合金的表面处 理中，传统的阳极氧化法与铬酸盐技术已经较为成熟，但阳极氧化法存在投资大、成本高的 缺点；铬酸盐技术中使用的六价铬是致癌物，各国和地区都实施了工业废水排放标准，严格 限制铬在金属表面处理中的使用[1-7].本文研究了一种不含铬的铝合金磷化液，对游离酸度、 温度、磷化时间和所含物质对磷化效果的影响进行了讨论，并通过 X 射线衍射、能谱仪、 扫描电镜和电化学等方法对磷化膜的成份、晶相、形貌、耐蚀性进行了研究. 1 实验方法 收稿日期 2