304不锈钢在察尔汗盐湖卤水中的腐蚀行为研究.pdf

304 不锈钢在察尔汗盐湖卤水中的腐蚀行为研究 董彩常 杨朝晖 钢铁研究总院青岛海洋腐蚀研究所 青岛 266071 摘要 用腐蚀挂片试验方法研究了304不锈钢在盐湖卤水中暴露2年的腐蚀行为，并运用室内电化学试验方 法研究了304不锈钢在卤水中的电化学行为。结果表明：室外卤水暴露2年后，304不锈钢腐蚀失厚为 0.0003mm/a，主要表现为点蚀，试样侧面加工缺陷处存在较深点蚀坑；室内电化学试验表明，304不锈钢卤 水中浸泡腐蚀16d之后，材料表面钝化膜局部被破坏，出现点蚀孔。 关键词 304不锈钢；盐湖；卤水；电化学；腐蚀 Research on corrosion behavior of 304 stainless steel in the brine of chaerhan saline lake DONG Cai-chang, Yang Zhao-hui Qingdao Research Institute for Marine corrosion, Central Institute for Iron and Steel, Qingdao 266071 Abstract The electrochemical characters and corrosion behavior of 304 stainless steel in the brine of saline lake were studied in this work by outdoor exposure experiment and indoor electrochemical experiment. The result indicated that the corrosion rate of 304 stainless steel in field brine was 0.0003mm/a after two-year exposure, and its corrosion behavior appeared mainly pitting corrosion character. Deeper pitting hole was found at the two sides of the sample due to machining defect. Electrochemical experiments showed that local surface of 304 stainless steel was destroyed after 16-day immersion in brine and formed pitting hole. Key Words 304 stainless steel, saline lake, brine, electrochemical, corrosion 在我国西部，盐湖数量多、资源丰富，仅青海省柴达木盆地就有盐湖 33 个，各种盐类 总储量达 2670 亿吨，盐湖矿产资源，尤其是液体（卤水）矿产资源的开发对振兴西部地区 的经济有重要的意义[1,2] 。不锈钢具有许多优良的性能，如耐蚀性、耐热性、耐低温性和好 的加工性能等，是开发利用盐湖卤水资源最基本的结构材料，然而，盐湖卤水的腐蚀会破坏 不锈钢的使用，危及设施、设备的安全正常运行。2007 年青海盐湖蓝科锂业股份有限公司 开工兴建，在生产试车期间发现，不锈钢设备出现了较严重的点蚀和缝隙腐蚀问题。目前关 于不锈钢在盐湖卤水中腐蚀行为的研究较少，黄桂桥等[3,4]首次研究了 304 不锈钢在卤水中 的动电位极化行为，得出 304 不锈钢的阳极极化曲线呈现钝化-活化特征，但是针对 304 不 锈钢在盐湖卤水中电化学腐蚀行为的详细研究却未见报道。 因此，本工作选择典型不锈钢材料（304 不锈钢），运用室外自然暴露试验和腐蚀电位 测量、线性极化测量、交流阻抗测量和动电位极化测量等室内电化学试验方法研究其在盐湖 卤水中的腐蚀行为。 1 实验方法 1.1 试验材料 试验材料为 304 不