无导向剂水热合成NaY型分子筛及其催化性能研究推荐.docVIP

无导向剂水热合成NaY型分子筛研究 摘 要 用最佳水热条件下NaY型分子筛负载Pd+，得到Pd/NaY催化剂，研究Pd/NaY催化剂对 关键词： Pd NaY 苯甲醇 氧化 Study of NaY synthesis by hydrothermol method without seed and its catalytic performance ABSTRACT Using sodium silicate and sodium aluminate as raw materials, NaY zeolites were synthesized by direct crystallization without seed gel. The hydrothermal synthesis conditions including aging time, crystallization temperature and time, water content andn(Na2O)/n(SiO2) in the system were investigated. The synthesized NaY were characterized by X-ray diffraction (XRD). The results indicate that increasing aging time favors the formation of more nuclears, but too long aging time leads to increase particle size of zeolite. High crystallinity NaY are synthesized when n(Na2O)/n(SiO2) and n(H2O)/n(Al2O3) are 1.0 and 160, respectively. The Pd/NaY were synthezied by impregnation of Pd2+ onto NaY. The catalytic performance of Pd/NaY was studied for the oxidation of benzyl alcohol to benzaldehyde. Keywords：Pd NaY benzyl alcohol oxidation 目 录 摘 要 I ABSTRACT II 第一章 文献综述 1 1.1 NaY分子筛的研究成果及发展前景 1 1.2 NaY分子筛的合成方法 2 1.2.1 酸浸偏高岭土-碱水热反应体系NaY分子筛的合成 2 1.2.2 导向剂法 2 1.2.3 NaY 分子筛的微波合成[8] 2 1.2.4无导向剂，以硅酸钠和铝酸钠水热直接合成NaY 3 1.3 苯甲醇液相氧化制苯甲醛催化剂的研究进展 3 1.3.1 负载型Ru基催化剂 4 1.3.2负载型Pd基催化剂 4 1.3.3 负载型Au基催化剂 5 7 2.1 NaY的制备 7 2.1.1 实验原料及仪器 7 2.1.2制备NaY的一般步骤 7 2.2 分组实验 7 2.2.1陈化时间对分子筛结构影响。 7 2.2.2 晶化时间对分子筛形貌和晶型的影响 8 2.2.3 晶化温度对分子筛结构的影响 8 2.2.4 n(Na2O)：n(SiO2)对反应的影响 8 2.2.5水含量对分子筛结构的影响 8 2.3 NaY的表征 9 2.4 催化剂的制备及催化性能 9 2.4.1 Pd/NaY的制备 9 2.4.2 Pd/NaY催化氧化苯甲醇。 9 实验结果与讨论 10 3.1 引言 10 3.2 结果与讨论 10 3.2.1 陈化时间对分子筛结构影 10 3.2.2 晶化时间对分子筛晶型的影响 11 3.2.3 晶化温度对分子筛结构的影响 11 3.3.4 n(Na2O)：n(SiO2)对反应的影响 12 3.3.5 水含量对分子筛结构的影响 13 3.8 Pd/NaY对苯甲醇氧化催化性能研究 15 3.8.1 最佳条件下制得的NaY及Pd/NaY样品的XRD谱图 15 3.8.2 苯甲醛的产率 15 结论与展望 17 参考文献 18 致谢 20 第一章 文献综述 1.1 NaY分子筛的研究成果及发展前景 Y型分子筛作为催化剂活性组元或者催化剂载体而广泛应用于催化裂化、加氢催化及异构化等炼油过程中。常规方法合成的Y型分子筛一般有1000nm左右的晶粒尺寸，已有研究表明，小晶粒尺寸的Y型分子筛由于具有较大的外表面积和较高的晶内扩散速率，在提高转化大分子能力、减少产物的二次裂化及降低催化剂结焦方面，表现出比常规晶粒尺寸Y型