20 11 年02 月 Feb．2011 第14 卷第02 期 Vol．14 No．02 防腐性能优异的新型环氧树脂固化剂 ———腰果酚改性聚酰胺 戴志晟，郭 铭 （卡德莱化工（珠海）有限公司北京技术服务中心，北京100070） 摘 要：分析了环氧树脂涂料用固化剂的现状，指出了其存在的问题。在此基础上开发了一种新型的腰果酚 改性酰胺树脂，从而解决了聚酰胺树脂低温无法固化和改性胺树脂的柔韧性差、易黄变等问题，是 一种具有优异防腐性能、能四季常温固化的高性能环氧树脂固化剂。 关键词：环氧树脂固化剂；腰果酚；聚酰胺；低温固化 中图分类号：TQ630.493 文献标识码：A 文章编号：1007－9548 （2011）02-0015－04 Excellent Anticorrosion Performance of New Epoxy Curing Agent-cardanol Modified Amide Dai Zhicheng, Guo Ming Abstract : The status of current epoxy curing agents was analyzed and the existing problems were pointed out in this paper. An novel cardanol modified amide resin was developed on the basis of this analysis. The problems which polyamide resin can not curing at low temperature and poor flexibility, easy to yellow and etc were dissolved. The curing agent is a high -performance epoxy resin curing agent which has excellent performance of anticorrosion and could be cured at room temperature in four seasons. Key words : epoxy resin curing agent, ceramide, amide, low temperature curing 1 环氧树脂固化剂的现状 性的产品，具有不同的性能特点，在不同的领域都得到 环氧树脂由于具有优异的黏结强度和防腐性能， 了广泛的应用。 在钢结构防腐领域得到了广泛的应用。而常温固化成 2 环氧树脂固化剂的特点 膜的产品是应用中的重点，从而也使环氧树脂用常温 上述的几类固化剂，虽都是常温固化剂，但具有不 固化剂的发展越来越迅速，产品种类越来越多。目前常 同的特性，应用领域各有不同，其主要特点如下。 用的常温固化剂主要是胺和改性胺类产品，小分子胺 聚酰胺类固化剂能与环氧树脂常温下固化成膜， 由于其挥发性大，毒性强，在使用中受到了限制，现已 固化后的漆膜具有良好的防腐性和柔韧性。但干燥时 基本不单独作为常温固化剂使用。现在主要的常温固 间长，其最大的缺点是低温固化性