合金元素对Au的强化效应与应用.docxVIP

Ξ合金元素对 Au 的强化效应与应用宁远涛 (昆明贵金属研究所 ,中国昆明 650221)Strengthening of Gold via Alloying ElementsNing Yuantao ( Kunming Institute of Precious Metals , Kunming 650221 ,China)Abstract :The characteristic of gold - rich phase diagrams in binary Au alloy systems ,the tendency ofdistribution and of strengthening of alloying elements in and to gold were summarized in present paper . The parameters of solid solution strengthening and precipitation strengthening of alloying elements to gold were analyzed. The light metals ,especially beryllium ,have the highest solid solution strengthening parameter ,whereas titanium has the highest precipitation strengthening parameter . The rare - earths have both parameters of high solid solution strengthening and high precipitation strengthening. The strengthening mechanisms of some practical gold alloys were discussed.Key words :Gold ; Gold alloys ; Solid solution strengthening ; Precipitation strengthening摘要 :本文讨论了二元 Au 合金系中富 Au 端相图特征 ,合金元素在 Au 合金中分布及强化与脆化倾向性 ,分析了合金元素对 Au 的固溶强化参数和沉淀强化参数 。轻金属 ( 尤其是Be) 具有最高固溶强化参数 , Ti 具有最高沉淀强化参数 ; 稀土金属兼具高的固溶强化参数 和沉淀强化参数 , 是强化 Au 与 Au 合金的重要合金元素 。讨论了某些实用 Au 合金的强化机制 。关键词 : Au ; Au 合金 ; 固溶强化 ; 沉淀强化中图分类号 : TG14613 + 1文献标识码 : A文章编号 : 1004 - 0676 (2002) 03 - 0051 - 061Au 与周期表元素反应的一般倾向性Au 与周期表中其它元素的合金化行为与这些元素在周期表中的位置有关 。一般地说 , 与 Au 最近邻的元素 , 如同族的 Ag 、Cu 及邻族的 Ni 、Pd 、Pt 等元素与 Au 形成连续固溶体 ; 在周期表中与Au 相距越远的元素 , 与 Au 形成固溶体的倾向性越小 , 而形成化合物甚至分凝的倾向越大 。因此 ,就其 Au 合金系富 Au 端相图特征而言 , 可将 Au 与周期表元素的合金化行为分为 7 个特征区 , 如图1 所示 。位于 Au 右边 2 区中的元素与 Au 形成下包晶反应区 , 即该区中元素加入 Au 中使 Au 熔点下 降并形成包晶 ; 位于 3 区中的元素则与 Au 形成上包晶反应区 (使 Au 熔点升高并形成包晶) ;位于 4 、5 、6 区中的元素与 Au 发生共晶反应 ; 而第 7 区中元素与 Au 不互溶 , 形成偏晶反应区 。文献 1将 Au - Zn 和 Au - Tl 系列入第 2 区内 , 但根据评估相图2 , Au - Zn 系的富 Au 端为共晶反应 ( 共晶Ξ 收稿日期 :2001 —09 —05 ,作者简介 :宁远涛 (1938 年～) ,男 ,教授 ,从事材料科学研究 。52贵 金 属第 23 卷温度 683 ℃) , 而 Au - Tl 系则为简单共晶 , 它们应属于第 6 区而非第 2 区 。图 1 是修正后的分类图 。图 1二元 Au 合金相图富 Au 端特征反应区分类Fig. 1Distribution of the characteristic reaction zones of gold - rich alloys in