快干型改性不饱和聚酯树脂的制备和性能研究 preparation and properties study of quick-drying modified unsaturated polyester resin.pdfVIP

绝缘材料 2013 ，46(3) 张春琪等：快干型改性不饱和聚酯树脂的制备和性能研究 41 快干型改性不饱和聚酯树脂的制备和性能研究 张春琪，顾健峰，周林江，徐晓风，丁 坤 （吴江太湖绝缘材料有限公司，江苏 吴江 215214 ） 摘要：采用自制M 改性不饱和聚酯和丙烯酸改性环氧树脂配制出快干型绝缘树脂，并与传统有溶剂绝缘树脂 和国外同类产品进行性能对比。结果表明：改性聚酯树脂可低温快速固化，其固化物具有介电性能优异、粘结 性好等优点，其干燥性、介电性能、储存稳定性等与国外同类产品相当，可以替代国外产品。 关键词：快干；低温；环保；无溶剂 + 中图分类号：TM215.4 1 文献标志码：A 文章编号：1009-9239（2013 ）03-0041-04 Preparation and Properties Study of Quick-drying Modified Unsaturated Polyester Resin Zhang Chunqi, Gu Jianfeng, Zhou Linjiang, Xu Xiaofeng, Din Kun (Wujiang Taihu Insulating Material Co., Ltd., Wujiang 215214, China) Abstract: A quick-drying insulating resin was prepared through self-made M modified unsaturated polyes- ter and acrylic acid modified epoxy, and then its properties were compared with that of the traditional sol- vent insulating resin and foreign similar product. The results show that the modified polyester resin can fast cure at low temperature, and the cured polyester resin has excellent dielectric property and good ad- hesive property. The drying properties, dielectric property and storage stability of the insulating resin are equivalent to the level of the foreign similar product, which can replace the foreign product. Key words: quick-drying; low temperature; environmental friendly; solventless 0 引 言 产品中溢出，造成产品起翘、爆壳、污染环境，对人 电子信息产业是国民经济的战略性、基础性支 体造成伤害。国外已经开始采用无溶剂绝缘漆替 柱产业，随着电子产业的迅猛发展，我国电子信息 代有溶剂绝缘漆，这种产品具有低温快固化、环保 产业的规模迅速扩大，产业结构不断优化，成为全 等特点。 球最大的电子信息产品制造基地。电子产品与人 常规无溶剂漆的固化温度偏高，一般固化温度 们生活起居息息相关，如电脑、手机、彩电、冰箱、空 高于120 ℃，即使能在低温固化，绝缘漆的使用期也 调、摄像机等消费性电子、电器产品，对产品提出了 偏短，很难满足工艺要求。采用自制M 改性不饱和 一系列安规认证，如UL 安规认证、VOC 安规认证、 聚酯和丙烯