含碳纳米管负载银纳米粒子的环氧树脂导热性能研究 陈立飞.docVIP

中国工程热物理学会 学科类别 工程热力学与能源利用 学术会议论文 编号：143765 含碳纳米管负载银纳米粒子的环氧树脂 导热性能研究 陈立飞，谢华清，杨蕾，于伟 （上海第二工业大学城市建设与环境工程学院，上海 201209） (0218536 lfchen@sspu.edu.cn) 摘 要： 关键词： Study on the thermal conductivity of epoxy resin containing carbon nanotube decorated by silver nanoparticles Lifei Chen, Huaqing Xie*, Lei Yang, Wei Yu School of Urban Development and Environmental Engineering, Shanghai Second Polytechnic University, Shanghai 201209, China (0218536 lfchen@sspu.edu.cn) Abstract: The hybrid thermal filler of carbon nanotube decorated by silver nanoparticles is prepared bulk and solventlessly. The effect of silver loading, filler content, and temperature on thermal conductivity of epoxy resin composites. Thermal conductivity of epoxy resin composites increase with increase of filler content, temperature, and silver loading. At 20oC as the silver loading and filler content is 1.5mol% and 0.1wt%, respectively, the thermal conductivity enhancement of epoxy resin composites is 102.45%. At 60oC and the same silver loading when the filler content is 5 wt%, the thermal conductivity enhancement of epoxy resin composites reach 341%. Key words: carbon nanotube, decoration, silver nanoparticle, epoxy resin, thermal conductivity 0引言 Fe2O3 and MgO)和碳纳米管的总含量为0.02wt%时，纳米流体的热导率提升约10%[10]。但是在制备过程中需要加入表面活性剂否则会发生沉淀。然而，Jha 等通过将金属纳米粒子分散在表面功能化的多壁碳纳米管表面，当Ag-MWNTs体积分数仅为0.03%时，水基纳米流体的热导率提升达37.3%，制备中不需要添加表面活性剂[11]。Zhang等研究表明，通过碳纳米管和金属纳米粒子之间的协同效应，当表面负载Cu纳米粒子的碳纳米管添加量为0.5wt%时聚乙二醇的热导率提升27%[12]。Chen等通过将表面负载银纳米粒子的多壁碳纳米管分散到水中，获得的流体导热性能也有很大提升[13] 。 本文中尝试将表面负载银的多壁碳纳米管分散到环氧树脂中，考察了复合物添加量、银的负载量及温度对环氧树脂导热性能的影响。 1 实验部分 S-4800扫描电子显微镜对制备的样品进行表征。所用多壁碳纳米管（MWNT）由深圳纳米港提供，醋酸银由国药化学试剂有限公司提供。 1.2 含碳纳米管负载银纳米粒子的环氧树脂复合材料制备和热物性测试 环氧树脂基复合材料的制备采用直接混合分散法，按一定的质量分数比例分别称取表面负载银纳米粒子的碳纳米管，再取适量的丙酮加入，超声振荡分散。然后再加入定量的环氧树脂，混合搅拌后再超声振荡分散。分散均匀后放入真空干燥箱