软锰矿浆烧结烟气脱硫研究及分析总结.docVIP

软锰矿烟气脱硫研究吴复忠，李水娥，金会心 （贵州大学 材料与冶金学院，贵阳 550025） 摘要：采用软锰矿烧结烟气进行脱硫。结果表明在软锰矿脱硫反应体系中存在以MnO2和SO2之间的氧化还原反应为主、SO2的催化氧化反应为辅的两种脱硫途径；后者对脱硫过程有着重要的影响，在软锰矿脱硫的反应体系中加入添加剂，对矿浆的pH进行调，能够显著改善脱硫效果和锰资源利用率。 关键词：软锰矿烧结烟气脱硫Study on Desulfurization of Sintering Flue Gas with Pyrolusite Slurry WU Fu-zhong, LI Shui-e, JIN Hui-xin (School of Materials and Metallurgy, Guizhou University, Guiyang 550025, China) Abstract: The experiment of desulfurization of sintering flue gas with pyrolusite was conducted. The results show that there are two desulfurization approaches in reaction system, i.e., mainly oxidation reduction between MnO2 and SO2, and secondary but significant catalytic oxidation reaction of SO2. The additives added in desulfurization system can improve desulfurization rate and utilization rate of manganese resources by regulating pH of pyrolusite slurry. Key words: pyrolusite; sintering flue gas; desulfurization “高炉—转炉”长流程钢铁企业的烧结是排放SO2的主要工序[1-3]。低硫原料配入法、高烟囱扩散稀释法、烟气脱硫法等烧结工序SO2排放[4]。烟气脱硫根据选择成本低、先进、效率高、脱硫的脱硫技术。软锰矿、菱锰矿烟气脱硫国内外关于软锰矿脱硫研究考查SO2、温度时间锰矿粒度、酸度等对浸出率的影响，而很少SO2转化利用率。烧结烟气脱硫菱锰矿作为调节pH的添加剂是一项“综合治理、变废为宝”的新工艺。 1 试验部分 1.1 试验原料 ，破碎磨细至粒度MnO2 35.20、SiO2 28.22、Al2O3 11.90、CaO 5.63、Fe 11.52、其他8.6。铁矿为某钢铁烧结SiO2 3.75%。焦粉灰分9.59水分11.5固定碳77.1动力煤灰分.86%、水分.66%、固定碳.35%）。 1.2 试验装置本试验的主要设备吸收塔示意图图1塔身为有机玻璃。；贵州省科技合作计划项目（黔科合外G字[2013]7001号）；贵州省科技重点攻关项目（黔科合GZ字[2011]3013）。 作吸收塔Fig.1 Sketch map of absorption tower 软锰矿浆从塔上部流入，回转窑焙烧烧结产生含的烟气从塔下部的入口进入进行逆流洗涤吸收吸收液循环气体中SO2含量矿浆pH吸收液中Mn2+含量、矿浆温度及吸收塔的进口烟气流量。 .3 试验数据处理及分析方法 采用SGA-94型测硫仪烟气中的矿浆中Mn2+浓度和pH、以及鼓入空气量，，计算公式11]。 2 结果分析与讨论 2.1 体系化学反应 在软锰矿矿浆烟气脱硫反应体系中，可能存在MnO2和SO2之间的氧化还原反应： （1） 以及SO2的催化氧化反应： （2） 烟气中SO2浓度~3 000 mg/m3温度20 ℃搅拌速度300 r/min液固比5∶1平均矿粉粒度mm、烟气流量m3/h、矿石MnO2含量35.20%矿浆总容积L。其中SO2烟气由动力煤焦粉和铁精矿按质量比∶2∶7混合焙烧产生图2 不同时间浸出液中Mn2+、SO42-含量 Fig.2 Content of Mn2+ and SO42- in lixivium different time 从图2可看出，软锰矿烟气脱硫体系中在不同的吸收时间范围内，浸出液中Mn2+、SO42-的含量不是按1∶1的比例发生变化，矿浆中的SO42-浓度高于Mn2+的浓度，并且循环矿浆的pH也在逐渐降低，说明液相中同时存在MnSO4和H2SO4两种产物。因此，矿浆中MnO2和S