_______________________________________________________________________________ 耐海水腐蚀低合金钢基体组织的探讨 1) 2) 2) 2) 宛农 ，范植金 ，曹全禹 ，刘正清 （1. 武汉工业学院机械工程系，武汉 430023 ；2. 武汉钢铁公司技术中心，武汉 430080 ） 摘要：采用加速腐蚀试验和力学试验测定了 6种低合金钢在海水中的腐蚀速率和力学性能， 重点考察了基体组织中珠光体数量的影响。结果表明：基体组织中珠光体百分比小于 9~12% 时，低合金钢耐海水腐蚀性能明显提高；而由珠光体数量减少所引起钢的抗拉强度或屈服强 度损失可由合金化途经来弥补。 关键词：耐海水腐蚀，低合金钢，基体组织 PROBE INTO MATRIX MICROSTRUCTURE OF SEAWATER CORROSION RESISTANT LOWER-ALLOYED STEEL WAN Nong1) ，Fan Zhijin2) ，Cao Quanyu2) ， Liu Zhengqing2) (1 Department of Mechanical Engineering ,Wuhan Polytechnic University, Wuhan 430023, China 2Technical Center, Wuhan Steel Iron Company, Wuhan 430080, China) ABSTRACT: Corrosion rates in seawater and mechanical properties of six kinds of lower-alloyed steels were measured by cycle corrosion test and mechanics test. The effects of percent pearlite in matrix structure was mainly investigated. It was found that the seawater corrosion resistance was obviously improved when the percent pearlite in matrix structure was decreased to 9-13% and its loss in tensile or yield strength caused by the reduction in percent pearlite was offset by the addition of alloy elements for a lower-alloyed steel. KEYWORDS: seawater corrosion resistance; lower-alloyed steel; matrix mirostructure C-Mn 系低合金钢因其具有良好的加 光体中铁素体—渗碳体之间易组成微电池 工、焊接和力学性能以及较低的成本而广泛 而导致钢的腐蚀速率上升[9] 。本研究在实验 用作舰船、钻井平台、桥梁和海港设施等结 室对基体组织中具有不同比例铁素体和珠 构材料。为改善 C-Mn 结构钢耐海水腐蚀性 光体含量的试验钢进行了加速腐蚀对比试 能和力学性能，国内外许多学者[1,2,3,4]研究 验和相关力学性能试验，以便为最终经济型 了合金化后钢中 Cr、Ni 、Mo 、Cu、P 和 Si 耐海水腐蚀用钢的最佳基体组织选择提供 以及稀土等合金元素的作用和影响，并在此 依据。 基础上形成了一系列耐海水腐