%9f阴极保护和阴极防护技术的状况与进展.pdfVIP

钢筋混凝土阴极保护和阴极防护技术的状况与进展 葛燕朱锡昶 (南京水利科学研究院南京210029) 摘要：盐污染环境中由于氯化物引起钢筋腐蚀导致钢筋混凝土结构过早破坏，是世界上普遍存在的现 象。对已建钢筋混凝土结构进行阴极极化以控制腐蚀的方法称为钢筋混凝土阴极保护技术，对新建钢筋混 凝土结构进行阴极极化以预防腐蚀的方法称为钢筋混凝土阴极防护技术。主要介绍钢筋混凝土阴极保护和 阴极防护技术的实施方法、状况与进展。 关键词：盐污染 钢筋混凝土 腐蚀 阴极保护 阴极防护 STATUSANDDEVELoPM匝NTOFCATHoDICPRoTECⅡoNAND CATHoDICPREVENlloNFORRE矾FoRCEDCONCR聊sTRUCrIJRES GeYahZhu Xiehang ResearchInstitute 210029) (N,mjingHydraulic N咖ing Abstraet：Itisthe thatconcretestructuresin∞l州contaminatedenvironments deteriomtion suffer phenomenon premature of concrete fromchlorideinduced corrosionTheme山ed cathodic structures reiaforcing applying polarization”theexisting for corrosionis calledcathodic Themethodof cathodic tothenewconcrete controlling pmtectjn applying polarization structuresfor is eMledcathodic It isinUxMucedthat and corrosion theconstructionmethod，status preventing prevention ofcathodic andcathodic forconcrete developmentprotection prevention eontarainationrejectedconcretecorrosioncathodic cathdic Ke”vords：salt protection prevention 可。许多国家还制定了有关的标准，为钢筋混凝土 0前言 结构有效实施阴极保护提供了技术依据。 钢筋混凝土结构是目前应用最为广泛的结构形 式。通常，混凝土具有高碱性．钢筋表面形成了一层 1国外钢筋混凝土阴极保护和阴极防护技术的发 薄的保护性氧化膜，该氧化膜使钢筋表面钝化，有效 展过程 地防止了钢筋的腐蚀。但在盐污染环境中，当钢筋 阴极保护可