锅炉管爆裂原因分 析.pdfVIP

第 42卷第3 期 包 钢 科 技 Vol .42,No .3 2016年6 月 Science and Technology of Baotou Steel June ,2016 锅炉管爆裂原因分析 刘 莉 ，李 智 丽 (内蒙古包钢钢联股份有限公司技术中心，内 蒙 古 包 头 014010) 摘 要 :通过对爆裂锅炉过热管进行宏观检查、金相检验、扫描电镜分析、力学性能检测，结果表明，爆裂锅炉过热 管在长期超温运行过程中产生蠕变，管体胀粗，管径增大，管壁减薄，且内壁产生腐蚀裂纹不足以承受管内蒸气的 压力发生爆裂。 关键词:过热管;爆裂;蠕变 中图分类号:TK223. 11 文献标识码： B 文章编号： 1009 -5 4 3 8 (2 0 1 6 )0 3 - 0 0 4 4 - 0 4 Cause Analysis on Bursting of Boiler Tube LIU Li，LI Z h i-li ( Technical Center of Inner Mongolia Steel Union Co. Ltd . of Baotou Steel( Group) Corp ., Baotou 0 1 4 0 1 0 , Monggol , China) Abstract The ： results of macro examination, metallographic examination, analysis with scanning electron microscope and mechanical property testing for superheater tube of bursting boiler indicate that it bursts since it is crept in such a long - term overheating operation that the tube expands,pipe diameter increases, tube wall thickness decreases and there is etch­ ing cracks on the inwall so that it cannot sustain the vapor pressure in tube. Key words superheater ： tube bursting ； creep； 12CrlM〇V 是我国使用广泛的珠光体耐热钢之 1 理 化 检 验 一，主要用于制造管壁温度小于580 °C 的锅炉过热 管，其内部是高温高压的蒸汽，外部受到高温烟气的 1 . 1 宏观检验 冲刷，工作环境十分恶劣。某厂用12C l M 〇V 制造 爆管的宏观形貌，如图1所示，爆裂管爆口处呈 的过热管，该管规格为038 m m X 4.5 m m ，管内蒸 喇叭口状，爆裂口开口宽度为55 m m ，开裂长度为 气温度约为500 C 。该 管 2007年开始服役，在 400 m m ，壁厚为3.5 m m ;开裂管两端钢管壁厚分别 2015年5 月发生爆裂，从投入使用到发生爆裂