高铬白口铸铁磨球的新工艺设计.pdfVIP

维普资讯 学兔兔 一 画 糍 铸造工艺 高铬白口铸铁磨球的新工艺设计 王仲珏， 刘冠岳 (安徽工程科技学院，安徽 芜湖 241000) 摘 要：高铬铸铁磨球显微组织应该由尽可能多的硬组织体、碳化物和马氏体组成，同时 应设法减少和控制零件中的内应力、显微裂纹及不连续性组织是新工艺的设计理念和目标。从 控制冷速、成分设计、铸造冶金处理、热处理等方面较为一致地体现了新工艺设计的原则。 关键词：高铬白口铸铁；磨球；工艺设计 中图分类号：TG252 文献标识码：A 文章编号：1673-3320(2008)02-0028-03 A New Technique Design of High Chrome White Cast Iron Grinding Balls WANG Zhongjue，LIU Guan—yue (Anhui University of Technology and Science，Wuhu 24 1 000，China) Abstract：A high chrome cast iron grinding balls microstructure should consist of as much as possible hard microstructure，carbide and martensite whose shape has noticeably changed by break offnet of carbide．Then to decrease and control inside stress．microcrack and nonconsistly organization in parts on design principle and goal of new technics。New principle of new technological design，conformabl~ from controlling cool rate，composition select，metallurgy and heat treatment，etc．are represented． Key聃 rds：High chrome white cast iron；Grinding ball；Technique design 与锻球、轧球相比，高铬铸铁冲击韧性低， 等对实现这一工艺设计目标极为有利。在控制冷 但是磨球在磨机中运行是呈瀑落式下滑冲击，属 速+成分设计+铸造冶金处理+热处理过程中应 小能量频繁冲击类型。而小能量多次冲击性能 高度一致地体现工艺设计的指导原则，并以此为 主要取决于材质的强度。与低铬白口铸铁磨球 据统一于为确定合理工艺参数而进行的试验设计 相比，高铬球具有较高的冲击韧性，这主要是因 和实施结果的综合指标考核体系中[2]。 为高铬白口铸铁的M C，型碳化物的三维开放式 骨架和如图1所示的碳化物呈条块状、菊花状分 布，每朵菊花是一个共晶团，菊花心部的碳化物 较小，从心部到边缘逐渐粗大。这比起对铸铁造 成脆性的宛如海绵状的渗碳体，里面镶嵌奥氏体 的转变产物的莱氏体型低铬白口铸铁使铸铁的 抗磨性和韧性明显提高[ 。结合大多的服役工况 条件，应将高铬铸铁磨球在获得高硬度的前提下 进一步提高韧性作为进行工艺设计的指导原则。 这样就