铸态高韧性球铁冷却壁的生产工艺.pdfVIP

维普资讯 学兔兔 铸 造 Jun．2008 FOUNDRY VO1．57 NO．6 · 632一 铸态高韧性球铁冷却壁的生产工艺 喻光远 (武铜机械制造有限公司，湖北武汉430083) 摘要：为了稳定获得铸态高韧性球铁高炉冷却壁，结合车间实际生产现状，通过对冷却壁化学成分的选择，原材料及 熔炼的控制，球化剂的选择，孕育剂及孕育方式的选择等关键技术的不断试验调整和改进，使生产的高炉冷却壁质量 可靠，性能优良，产品合格率达98％以上。 关键词：高炉冷却壁；铸态高韧性球铁；厚大端面球铁件 中图分类号：TG255 文献标识码：B 文章编号：1001—4977(2008)06-0632-02 Production Technique of AsCast High Toughness Ductile Iron Cooling-Wall Y U Guang—yuan (Machinery Manufacturing Limited Liability Company of WISCO，Wuhan 430083，Hubei，China) Abstract：High—toughness ductile I ron cooling-wall is a main part of the large—sized blast furnace．To produce consistently the ductile I ron with better quality under the existing workshop conditions，some key factors influencing the product。S quality and properties，such as chemical composition，raw materials，melting parameters，nodulizer，inoculants and inoculating method，etc．were adjusted properly and improved through trials，As a result，the cooling wall with high quality and better properties were obtained and the qualified products came to more than 98％． Key words：blast furnace cooling wall；as—cast high—toughness ductile iron；heavy section ductile iron casting 高韧性球铁冷却壁是现代化大型高炉的主要冷却 大断面冷却壁，硅应严格控制，硅量过高易生成碎块 部件，与灰铸铁冷却壁相比它具有抗热振性好、机械 状异形石墨，提高低温脆性，降低球铁强度和伸长率， 强度高、伸长率高、使用寿命较长等优点，被称为 且随硅量增加，球铁导热系数降低。综合考虑：选择 “长寿冷却壁”。目前，国内外1 000 rrl 级以上高炉大都 碳当量4．2~4．5％，3．4％～3