酯硬化水玻璃砂溃散性的研究.pdfVIP

学兔兔 酯硬化水玻璃砂溃散性的研究 赵丽娟 (齐齐哈尔车城化工生产公司，黑龙江 齐齐哈尔 161002) 摘要：针对酯硬化水玻璃砂的实际应用情况，采用正交试验分析了KOH、溃散剂、增强剂对型 砂溃散性的影响。结果表明，K0H、溃散剂及增强剂中，溃散剂的加入量对酯硬化水玻璃砂溃 散性的影响是最大的。最佳工艺条件为KOHT)~ 量5％，溃散剂加入量6％，增强剂加入量0．1％。 关键词：酯硬化水玻璃砂；抗压强度；溃散性 中图分类号：TG221 ．2 文献标识码：A 文章编号：1673—3320(2015)03—0016-02 Research on Collapsibility of Ester Cured Sodium Silicate Sand ZHAO LUuan (Qiqihar Checheng Chemical Industry Co．，Qiqihar 1 61 002，Heilongjiang，China) Abstract：Based on the practica1 application of ester cured sodium silicate sand the effects Of K0H．break． down agent and strengthening agent on the collapsibility of molding sand were analyzed by orthogonal experiment．The results show that among KOH，break—down agent and strengthening agent。the addition of break—down agent is the biggest impact on the collapsibility of ester cured sodium silicate sand．The best process conditions is 5％ for KOH．6％ for break-down agent and 0．1％ for strengthening agent． Kev words：ester cured sodium silicate sand；compressive strength；collapsibility 我国铸钢件生产主要采用水玻璃砂工艺。水 玻璃 (搅拌1 min)一出砂。 玻璃的价格便宜、供应充沛，水玻璃砂在混砂、 抗压强度： 50 mm×50 mm圆柱形标准试 造型、浇注和落砂过程中均无刺激性气味或有毒 样，三锤法紧实成形；马弗炉升温至1000℃，试 气体产生，也无黑色污染，但其存在溃散性差， 样保温20 min后冷却至室温，进行抗压强度试验。 落砂异常困难，清砂超时的难题【”。本文初步分 抗拉强度：“8”字形标准试样，三锤法紧实 成形；24 h后进行抗拉强度试验。 析了对水玻璃砂强度影响最大的因素，提出了在 硬化条件：室温 (20℃)下自然硬化。 保证抗拉强度的情况下，提高水玻璃砂溃散性的 1．3 正交试验表设计 有效方法。 为分析KOH、溃散剂和增强剂加入量对水玻 1 试验方法 璃砂强度的影响，设计了三因素三水平的正交