学兔兔 2011年第6期 混凝土与水泥制品 201l N06 6月 CHINA CONCRETE AND CEMENT PRODUCTS June 聚乙烯醇纤维增韧水泥基复合材料研究进展 徐涛智 ，杨医博 ，梁颖华 ，郭文瑛 (1．华南理工大学土木工程系，广州510640； 2．华南理工大学亚热带建筑科学国家重点实验室，广州510640) 摘 要：聚乙烯醇纤维增韧水泥基复合材料 (Polyvinyl alcohol Fiber—Engineered Cementitious Composites简称 PVA-ECC)是一种拉伸变形性能优异的水泥基复合材料，是通过断裂力学和微观力学原理对材料体系进行系统设 计和优化得到的复合材料。本文介绍了国内外PVA—ECC的研究情况，并对国产PVA纤维无法应用于PVA—ECC 的原因以及PVA—ECC直接拉伸实验方法两个亟待解决的问题进行了论述。 关键词：聚乙烯醇纤维；PVA—ECC；增韧；直接拉伸 Abstract：Polyvinyl Alcohol Fiber—Engineered Cementitious Composites (PVA—ECC)is a kind of cement-based composite material with extraordinary tensile deformation performance，which is a composite material systemically designed and optimized by fracture mechanics and micro～mechanics principles．The research situations of PVA—ECC in China and abroad are introduced。and two waiting solving problems such as the reason that PVA fiber cannot be applied to PVA— ECC in China and the direct tensile testing method for PVA—ECC are discussed． Key words：Polyvinyl alcohol fiber；PVA—ECC；Enhanced toughness；Direct tension 中图分类号：TU528．58 文献标识码：A 文章编号：1000-4637(201 1)06-39-06 0 前言 荷载作用下仍会发生应变软化破坏。传统的高性能 聚乙烯醇纤维增韧水泥基复合材料(Polyvinyl 纤维增强水泥基复合材料是通过体积掺量大于5％ alcohol Fiber-Engineered Cementitious Composites， 的钢纤维来实现材料的高韧性和高抗拉强度的，该 简称PVA—ECC)是一种拉伸变形性能优异的水泥 复合材料在直接拉伸作用下能表现出明显的准应 基复合材料，最早是由美国密歇根大学的Victor C． 变硬化特性，但由于纤维掺量太高，必须运用特殊 Li教授和麻省理工大学的Christopher K．Y．Leung 的搅拌和施工工艺。同时，高掺量的钢纤维也加大 教授于1992年提出来的，是利用断裂力学和微观 了工程造价，使应用范围受到限制。 力学原理，对材料体系进行系统地设计、调整和优 Li和Leung教授提出聚乙烯醇纤维增韧水泥 化得到的复合材料l1]。PVA—ECC主要用