优秀毕业论文（设计）_磺酸掺杂苯胺-邻乙氧基苯胺共聚物的合成优化及性能研究.docVIP

摘要 以苯胺、邻乙氧基苯胺为单体，过硫酸铵为氧化剂，磺基水杨酸为介质酸，采用化学氧化法合成苯胺-邻乙氧基苯胺共聚物。固定反应温度为0℃，探讨了反应时间、氧化剂用量、介质酸用量、单体摩尔配比对共聚物电导率的影响，得到最佳合成条件：0℃；9h；氧化剂与共聚单体物质的量比1:1；介质酸与共聚单体物质的量比1:1；苯胺与邻乙氧基苯胺单体的摩尔配比1:1。对最佳条件下合成的共聚物及聚苯胺、聚邻乙氧基苯胺进行FT-IR、UV-Vis、TG、电导率、溶解度的分析研究，结果表明，共聚物与聚苯胺的化学结构相似，苯胺与邻乙氧基苯胺共聚能够有效提高聚苯胺的溶解性和热稳定性，从而改善其加工性能。与聚苯胺相比，共聚物的电导率有所降低。 关键词：苯胺邻乙氧基苯胺共聚掺杂 Abstract By microemulsion polymerization method using aniline(An) and O-ethoxyaniline(OEA) as monomers, ammonium persulfate(APS) as the oxidant and as the Sulfosalicylic acid as the medium acid.We set the temperature to zero degrees and analysed how the time,the quantity of Oxidant,the concentration of hydrochloric acid and the ratio of monomers effect on product’s property.To get the best reaction condition :0℃;9h;the ratio of anmmonium persulfate and the monomers is 1:1;the ratio of medium acid and the monomers is 1:1;the ratio of aniline and o-phenetidine is 1:1.Analysis of FT-IR,TG,UV-Vis,electrical conductivity and solubility of polyaniline and poly-o-aniline under optimum conditions..By the analysis shows that the copolymer is similar to the chemical structure of polyaniline,polymerization of aniline and o-phennetidine could improve poiyaniline’s solubility and heat endurance,so as to improve its processability. Compared with poly aniline,copolymer’s conductivity is low. Key Words: Aniline O-phenetidine Copolymerization Doping 目录 1. 前言 1 1.1 聚苯胺的发展史 1 1.2 聚苯胺的结构和性能 3 1.3 聚苯胺衍生物的理论研究 4 1.3.1 环上取代衍生物 4 1.3.2 氨基氮上取代衍生物 5 1.4 论文研究依据及内容 5 2. 实验部分 7 2.1 试剂及仪器 7 2.2 实验内容 7 2.2.1 前期准备 7 2.2.2 磺酸掺杂苯胺-邻乙氧基苯胺共聚物的合成 8 2.3 性能测试 8 2.3.1 溶解度测试 8 2.3.2 红外光谱测试 9 2.3.3 TG测试 9 2.3.4 UV-Vis吸收光谱测试 9 2.3.5 电导率测试 9 3. 结果与讨论 10 3.1 实验数据及分析 10 3.1.1 优化反应时间 10 3.1.2 优化介质酸用量 10 3.1.3 优化氧化剂用量 11 3.1.4 优化单体摩尔配比 12 3.2 红外光谱对比分析 12 3.3 UV-Vis光谱对比分析 13 3.4 TG对比分析 14 3.5 电导率对比分析 15 3.6 溶解度对比分析 15 4. 结论 17 参考文献 18 谢 辞 19 1. 前言1.1 聚苯胺的发展史 自1977年发现导电聚乙炔以来，导电聚合物以其新颖的物理化学性能和广阔的应用前景而备受物理学、化学和材料科学家的关注。目前研究较多典型的高聚物有聚对苯(PPP)、聚吡咯(PPY)、聚噻