采用氧化剂和交联剂提高羽绒蓬松度的研究.docVIP

采用氧化剂和交联剂提高羽绒蓬松度的研究 　　摘要：根据羽绒的特性，通过氧化法和交联法提高羽绒的蓬松度。选用次氯酸钠作为氧化剂和醛类交联剂WS对羽绒进行蓬松处理，根据FZ/T80001―2002《水洗羽毛羽绒试验方法》检测羽绒蓬松度变化情况。采用单因素优化出最佳应用条件为：次氯酸钠用量1.2g/L，在50℃氧化处理60min后，进行交联处理，交联剂WS用量1.5g/L，前期预交联pH值4.5，交联处理终点pH值6.5，交联温度50℃、时间40min，此时羽绒的蓬松度提高显著。关键词：羽绒；蓬松度；氧化处理；交联处理 　　中图分类号：TS 195.6 　　文献标志码：A Research on Enhancing Fill Power of Down by Oxidizing Agent and Crosslinking Agent 　　Abstract： In this paper， natural down was treated by oxidizing agent（NaClO） and crosslinking agent（WS） to improve its fill power. The dosage of agents and reaction conditions were studied through single factor experiment. The results showed optimal conditions were as follows： in oxidation reaction， the dosage of NaClO 1.2 g/L， temperature 50 ℃， time 60 min； in crosslinking reaction， the dosage of WS 1.5 g/L， initial pH value 4.5， final pH value 6.5， temperature 50 ℃， time 40 min. The fill power of nature down increased obviously after being treated by the optimal process. 　　Key words： down； fill power； oxidation treatment； crosslinking treatment 　　羽绒是长在鹅、鸭的腹部，成芦花朵状的绒毛，其具有质地轻软、蓬松和保暖隔热的性能。羽绒品质的好坏由绒子含量、蓬松度、残值率等因素决定。其中，蓬松度的高低反应了羽绒的弹性、填充力以及保暖性能。羽绒蓬松度的高低对羽绒品质有很大影响，但是关于提高羽绒蓬松度的加工工艺鲜有研究报道。本文拟采用氧化剂和交联剂处理羽绒，以期提高羽绒的蓬松度。 　　1 实验内容 　　1.1 实验准备 　　材料：含绒量90%的羽绒，由东隆羽绒制品有限公司提供。 　　药品及助剂：次氯酸钠、甲酸、小苏打均为分析纯；渗透剂、交联剂WS为工业品。 　　仪器：恒温水浴振荡器（金坛市金城国胜实验仪器厂），电子天平（凯托称重设备有限公司），小型羽绒甩干烘干机（杭州良机羽绒设备有限公司）。 　　1.2实验工艺及测试方法 　　称取一定量的羽绒，经2%的洗涤剂水洗30min、漂洗30min后，加入氧化剂、交联剂处理，甩干、烘干后，检测羽绒蓬松度，考察羽绒蓬松度的变化情况。 　　（1）优化次氯酸钠氧化剂的工艺 　　取样（60g羽绒）→水洗（2%的洗涤剂，2kg水，50℃，振荡30min）→漂洗（搅动，常温漂洗30min）→氧化处理（2kg水，氧化剂Xg/L，温度Y℃，转动Zmin）→漂洗（3min）→甩干（10min）→烘干（120℃，10min）→冷却（10min）→打包。 　　（2）优化交联剂WS的工艺 　　取样（60g羽绒）→水洗（同上）→漂洗（同上）→氧化处理（2kg水，氧化剂1.2g/L，温度50℃，转动60min）→交联（交联剂Wg/L，温度S℃，转动Nmin）→漂洗（同上）→甩干（同上）→烘干（同上）→冷却（同上）→打包。 　　1.3蓬松度检测方法 　　各国测量蓬松度的方法及产品合格的判定标准不尽相同，但是蓬松度的测试原理都为一定重量的羽绒，在一定压力下占有的空间体积大小。 　　本文按照FZ/T80001―2002《水洗羽毛羽绒试验方法》测定羽绒蓬松度。将样品氧化、交联处理后，抖入前处理箱中，在相对湿度（65%±2%）、温度（20±2）℃的环境中放置24h后，再称取28.5g样品抖入蓬松仪（图1）内，盖上铝箔片，静置1min后读取刻度。 　　2结果与讨论 　　2.1氧化剂次氯酸钠对羽绒蓬松度的影响