AMCI迁移型防腐阻锈剂的性能研究.docVIP

AMCI迁移型防腐阻锈剂的性能研究 贺奎，王二坡，李海峰，夏义兵，王靖 （北京市建筑工程研究院，北京，100039） [摘要] 钢筋腐蚀成为当今世界影响混凝土耐久性的主要因素,特别在氯盐环境中,钢筋腐蚀是首要因素。文中简要介绍了北京市建筑工程研究院自主研发的AMCI迁移型防腐阻锈剂的抗氯离子侵蚀性能，通过新拌砂浆法、溶液浸泡法以及干湿冷热循环等试验，显示AMCI具有良好的抗氯离子侵蚀作用和一定迁移作用。 [关键字] 钢筋混凝土 耐久性 氯盐侵蚀 AMCI 迁移性 [中图分类号] [文献标识码] [文章编号] Property research of a kind of migrating corrosion inhibitor-AMCI He Kui, Wang Wan-jin, Li Hai-feng, Xia Yi-bing,Wang Jing (Beijing Building Construction Research Institute, Beijing, 100039) Abstract: The corrosion of steel bars in concrete has become the major cause that influences the durability of concrete. In this paper, the properties of AMCI corrosion inhibitor, developed by BBCIR (Beijing Building Construction Research Institute) independently, was studied. By a series test based on YB/T9231-98, it was evidenced that AMCI can reduce the corrosion rate of steel reinforcements embedded in a hardened concrete structure. It was also investigated that AMCI has migrating ability. Keywords: reinforced concrete, durability, corrosion caused by chloridion, AMCI, migrating ability [前言]钢筋混凝土作为一种结构材料,广泛地应用在桥梁、建筑物、高架桥、堤坝、海底隧道和大型海洋平台等结构中。混凝土的耐久性直接决定了建筑物的安全使用寿命[1]。在影响钢筋混凝土耐久性的诸多因素中, 钢筋在混凝土中的腐蚀破坏是首要因素[2]。混凝土钢筋锈蚀破坏已成为世界范围内的严峻性课题。 控制混凝土钢筋腐蚀的方法有很多,如采用耐蚀钢筋、阴极保护法、涂(镀) 层钢筋和钢筋阻锈剂法等[3]。钢筋阻锈剂(Rebar Corrosion Inhibitor)是能阻止或减缓钢筋腐蚀的化学物质,通常可以通过掺加到混凝土中或涂敷在混凝土的表面而起作用[4]。欧洲标准化委员会(European committee for Standardization，CEN)在PR ENV1504—9标准中确认使用迁移型阻锈剂是一种有效的腐蚀控制方法。 北京市建筑工程研究院利用现有技术优势合成开发出一种新型迁移性阻锈剂-AMCI钢筋混凝土阻锈剂。AMCI具有优良的抗氯离子锈蚀性能，并通过了国家权威部门的检测。 试验部分 1.1 AMCI迁移型防腐阻锈剂抗氯离子锈蚀试验 1.1.1新拌砂浆法 按照GB 8076-1997《混凝土外加剂》附录B中钢筋锈蚀快速试验方法（新拌砂浆法）来模拟钢筋在混凝土中的锈蚀情况。 试验中所用灰砂比为1:2，W/C为0.5，分别测定下列几种情况的电位： a普通正常砂浆； b拌和用水为5%氯化钠溶液； c拌和用水为5%氯化钠溶液，胶材用量2%掺入AMCI混凝土钢筋防腐阻锈剂。 原材料的选择 水泥：基准水泥 砂：ISO标准砂 氯化钠：分析纯 水：纯净水 组锈剂：AMCI 1.1.2溶液浸泡法 参照YB/T 9231-98《钢筋阻锈剂使用技术规程》，我们对此试验方法进行设计： 锈蚀试件：将Q235钢车成的，直径为10mm、长50mm，表面粗糙度达到Ra6.3μm的圆柱形钢筋试样改用等表面积的（2cm×4cm×0.1cm）Q235钢板裁成的表面粗糙度Ra6.3μm的钢片，便于锈蚀情况的观察； 腐蚀溶液：将15%NaCl的饱和Ca（OH）图1新拌砂浆恒电流、电位与时间曲线图 图1为新拌砂浆恒电流、电位与时间曲线图，从图中可以看出，正